Thermoplastic elastomers

ABSTRACT

TPE&#39;s which comprise A blocks or B blocks or both A blocks and B blocks, which are crystalline and in which at least a part of the crystallinity result from the presence of crystallizable side chains. Such crystalline blocks are referred to as SCC blocks. TPE&#39;s containing SCC A blocks are novel and as such form part of the present invention. The invention also includes processes, compositions, shaped articles and assemblies which make use of TPE&#39;s containing SCC A blocks.

GOVERNMENT SUPPORT

The U.S. Government may have certain rights to this invention pursuant to U.S. Air Force Contract No. FO8635-90-C-0350.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of Ser. No. 08/048,280 filed Apr. 14, 1993, U.S. Pat. NBo. 5,665822, and a continuation-in-part of

(a) Ser. No. 07/773,047 filed Oct. 7, 1991, by Bitler, Stewart, Kamp and Freelin (now abandoned);

(b) Ser. No. 07/957,270 filed Oct. 6, 1992, by Bitler, Stewart, Kamp, Freelin and Yoon (now abandoned), as a continuation-in-part of Ser. No. 07/773,047; and

(c) Ser. No. 07/885,915 filed May 18, 1992, by Stewart (now U.S. Pat. No. 5,254,354) as a continuation of Ser. No. 07/623,602 filed Dec. 9, 1990, by Stewart, now abandoned.

This application is also related to

(d) Ser. No. 07/654,723 filed Feb. 12, 1991, by Schmitt and Tsugita (now abandoned);

(f) Ser. No. 07/928,800 filed Aug. 12, 1992, by Schmitt, Tsugita, Clarke, Bitler, Larson and Schultz as a continuation-in-part of Ser. No. 07/829,494; and

(g) Ser. No. 07/939,100 filed Sep. 2, 1992 by Schmitt (now U.S. Pat. No. 5,469,867).

The disclosure of each of the patents referred to above is incorporated herein by reference for all purposes.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to thermoplastic elastomers.

2. Introduction to the Invention

Thermoplastic elastomers, which are often referred to as TPE's, are well known. The TPE's in general use contain (i) polymeric blocks (usually referred to as "hard" blocks or A blocks) which (a) are amorphous and have a second order transition point, T_(gh), which is well above room temperature, or (b) have a crystalline polymer backbone and have a crystalline melting point, T_(mh), which is well above room temperature, and (ii) amorphous polymeric blocks (usually referred to as "soft" blocks or B blocks) which have a glass transition point, T_(gs), which is well below room temperature. Each soft block is linked to at least two hard blocks, so that at temperatures between T_(gs) and T_(mh), or T_(gs) and T_(gh), the amorphous B blocks are tied together, resulting in elastomeric behavior. Above T_(mh) or T_(gh), melting or softening of the hard blocks permits viscous flow of the polymeric chains, resulting in thermoplastic behavior. Known TPE's are described for example in U.S. Pat. Nos. 4,260,659 (Gobran), 4,361,526 (Allen), 4,483,978 (Manser), 4,551,388 (Schlademan), 4,554,324 (Husman), 4,656,213 (Schladman), 4,764,586 (Manser), 4,778,852 (Futamura), 4,806,613 (Wardle), 4,919,737 (Biddle et al), 4,952,644 (Wardle et al), and 4,976,794 (Biddle et al) and in the articles in Polymer, 29 (7), 1233-1239 (1988) Kallitsis et al; J. Appl. Poly. Sci 37 (1), 267-281 (1989) Murphy et al; J. Poly. Sci, Part A, Poly Chem, 28 (9) 2393-2401 (1990) Talukder et al; Makromol Chem, 190, 1069-1078 (1989) Khan et al, 191, 603-614, 615-624, and 2341-2354 (1990) Fakirov et al, and 191 2355-2365 (1990) Gogeva; and Macromolecules 18 (2), 123-127 (1985) Miyamoto et al, and 23, 333-337 (1990) Chow. The disclosure of each of those patents and articles is incorporated herein by reference.

It has also been proposed in the patent literature to use, as components in temperature-sensitive dispensers for pesticides, disinfectants, drugs and other active agents, block copolymers containing a side chain crystallizable (SCC) polymer and a second polymer which exhibits a glass transition or melting point higher than the SCC polymer, such that the entire mass exhibits mechanical stability above the melting point of the SCC polymer but below the transition of the second polymer. See U.S. Pat. No. 4,830,855 (Stewart), the disclosure of which is incorporated herein by reference. The block copolymer undergoes a rapid change in permeability to the active agent in the region of the melting point of the SCC polymer, and the second polymer ensures that the SCC polymer remains immobilized even if its melting point is reached or exceeded.

SUMMARY OF THE INVENTION

This invention relates to TPE's which comprise A blocks, or B blocks, or both A blocks and B blocks, which are crystalline and in which at least a part of the crystallinity results from the presence of crystallizable side chains. Such crystalline blocks are referred to herein as SCC blocks. TPE's containing SCC A blocks are novel and as such form part of the present invention. The invention also includes processes, compositions, shaped articles and assemblies which make use of TPE's containing SCC A blocks. TPE's containing SCC B blocks and non-SCC A blocks are not novel as a class, but this invention includes a wide range of novel processes, compositions, shaped articles and assemblies which make use of such TPE's.

TPE's Containing SCC A Blocks

TPE's containing SCC A blocks have the advantage that they can exhibit a much more rapid change in viscosity in the region of the crystalline melting point of the side chains in the TPE (referred to herein as T_(q)) than is exhibited by known TPE's in the region of T_(mh) or T_(gh). This rapid change in viscosity results in a number of important advantages. One advantage is that the novel TPE's can be melt processed at temperatures not far above T_(q), e.g. below about (T_(q) +10)° C., whereas known TPE's are typically melt processed at temperatures at least 40° C. above T_(mh) or T_(gh). Known TPE's are typically melt processed at temperatures above 100° C., whereas the preferred TPE's of the invention can be melt processed at temperatures below 100° C., for example below 75° C. and even below 50° C. This is particularly useful when the TPE is preferably or necessarily maintained at a temperature below a critical limit (referred to herein as T_(crit)). Such conditions arise for example when the TPE is associated with (e.g. is contained within, surrounds, forms a layer on, or is mixed with) a thermally responsive substance which may undergo, at a temperature above T_(crit), a change which is undesirable during such processing. The substance may be for example in the form of (i) solid particles dispersed within the TPE, e.g. particles of an explosive solid, or a pharmaceutical or agricultural chemical, or (ii) a substrate which is contacted by the TPE, e.g. a vessel in a living animal into which the TPE has been injected or otherwise placed, or (iii) a solid or a liquid which is encapsulated by the TPE. Another advantage is that the novel TPE's can be used as carriers (including encapsulants) for substances which are at least partially protected by the TPE at temperatures substantially below and approaching T_(q). The protection may be against physical attack and/or against chemical attack. The hard blocks in the TPE will begin to melt at a temperature T_(o) which is somewhat below T_(q), e.g. 3°-12° C. below T_(q). As the temperature is increased from T_(o) to T_(q), there is a rapid change in the protection provided by the TPE, and above T_(q) the substance may be released entirely from the TPE. For example, a mixture of the TPE and an agricultural chemical can be applied during a cold season of the year while the ambient temperature is below T_(q) and the chemical will be released when the ambient temperature exceeds T_(q). Similarly a seed can be coated with a TPE and will not germinate until the ambient temperature approaches or exceeds T_(q).

Another very important advantage of the novel TPE's containing SCC A blocks is that the value of T_(q) can be closely controlled through selection of the crystallizable moieties in the side chains. Thus, for a given crystallizable moiety, T_(q) is mainly dependent on the length of the crystallizable moiety, and changes by at most a few °C., e.g. less than 5° C., with changes in the molecular weight of the A block. In the known TPE's, by contrast, T_(mh) or T_(gh) changes substantially with changes in the molecular weight of the A block, because the melting point is dependent on folding of the main chain. In the TPE's containing SCC A blocks, it is possible to change the physical properties of the TPE, e.g. the elongation, modulus and tensile strength, without substantially changing T_(q), by changing the molecular weight of the TPE and/or the molecular weight of the A blocks and/or the relative amounts of the A and B blocks.

The TPE's containing SCC A blocks also show a relatively small difference between T_(q) (the endotherm melt peak on a DSC curve as the TPE is heated) and the crystallization peak on a DSC curve as the molten TPE is cooled.

Another very important advantage of the novel TPE's containing SCC hard (A) blocks is that the presence of the SCC A blocks results in improved shear strength. Furthermore their shear strength can be yet further improved by incorporation therein of a relatively low molecular weight and low melting crystalline additive, particularly an SCC polymer. The crystalline additive must be intimately mixed with the TPE, preferably through a melt mixing process or a process which comprises mixing the TPE and the additive in a common solvent. Particularly good results are obtained when the SCC blocks in the TPE and in the additive are structurally similar, and it appears that the improved shear strength results from co-crystallization of the additive and the SCC blocks. Thus a preferred combination is a TPE containing SCC blocks comprising polymethylene or poly (substituted methylene) groups and an SCC additive comprising polymethylene or poly (substituted methylene) groups. Suitable crystalline additives include those disclosed in the Schmitt et al Application Ser. No. 07/928,800 incorporated by reference herein, now U.S. Pat. No. 5,412,035.

The advantages noted above make the novel TPE's with SCC hard blocks, and mixtures thereof with crystalline additives, particularly suitable for use as pressure-sensitive adhesive (PSA's) and as hot melt adhesives. The TPE, or mixture thereof with a crystalline additive, can be the sole polymeric ingredient(s) of the adhesive, or can be mixed with other polymeric ingredients. For example, a conventional PSA can be modified by addition of the TPE or mixture of TPE and additive. The adhesive preferably contains 25 to 100%, particularly 75 to 100% of the TPE, and 0 to 50%, preferably 1 to 40%, of the additive. PSA's for use in the medical field for attachment to human skin preferably contain 20 to 35% of the additive. PSA's for use in other fields preferably contain less than 15%, e.g. 1 to 5%, of the additive. The adhesive can also contain additives such as tackifiers, plasticizers, fillers, stabilizers and pigments. PSA's which contain the crystalline additive have the valuable property that they have reduced adhesive strength when heated to temperatures approaching or above the crystalline melting point of the additive, as discussed in Schmitt et al Application Ser. No. 07/928,800, U.S. Pat. No. 5,412,035.

The novel TPE's containing SCC hard blocks can also contain SCC soft blocks. We have found that such TPE's, in addition to the advantages noted above for TPE's containing SCC hard blocks, are particularly useful in the form of films and other shaped articles which are heat-sealed to other polymeric articles. The TPE will undergo a rapid change in its physical properties, including its permeability to at least some gases and vapors, e.g. O₂, CO₂ and water vapor, in the region of T_(ms), but will retain substantial strength until heated to a temperature in the region of T_(q), when it will again undergo a rapid change in its physical properties, including its heat sealability. The repeating units of the different SCC blocks can be selected to provide a change in permeability (or other property) over a desired temperature range, and to provide a hard block which, above T_(mh), will be compatible with the other polymeric material to which the TPE is to be heat sealed. In this way, it is possible to make a TPE which is sufficiently flexible at 0° C., which undergoes a marked change in permeability in the range of 0° C. to 40° C., which retains adequate physical strength at temperatures up to T_(q) (or close to it) and which can be melt extruded and heat sealed at temperatures not far above T_(q), e.g. 60° to 100° C.

If desired, the physical strength of the TPE can be improved by crosslinking, but this is not generally necessary. Such a TPE can be particularly useful as a packaging material, e.g. for actively respiring biological material, as disclosed in the Stewart Application Ser. No. 885,915 incorporated by reference herein, now U.S. Pat. No. 5,284,354.

TPE's Containing SCC B Blocks and Non-SCC A Blocks

We have found that SCC soft (B) blocks can confer important and previously unrealized benefits on TPE's containing them, making it possible to use such TPE's in ways which are novel and surprisingly valuable, even when the A blocks are not SCC blocks and the TPE is in itself known for use in other ways. For example, such TPE's can be used to provide pressure-sensitive adhesives (PSA's) with very valuable properties, to provide films and other shaped articles which can be heat-sealed to other articles, and to provide hot melt adhesives.

Summary of Various Aspects of the Invention

First Aspect--Novel TPE's

In a first aspect, this invention provides novel TPE's containing SCC hard (A) blocks. These novel TPE's preferably comprise polymeric molecules which comprise

(i) polymeric A blocks which

(a) are crystalline and have a melting point T_(q), and

(b) wherein at least one of the A blocks comprises a side chain comprising crystallizable moieties which render the block crystalline; and

(ii) at least one polymeric B block which is linked to at least two A blocks and which

(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C., or

(b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C.

Second Aspect--Processes for Preparing the Novel TPE's

Any process can be employed to make the novel TPE's of the present invention. However, particularly useful processes, which provide the second aspect of the present invention, comprise

I . reacting together

(i) an A block precursor which is the A block containing at least one reactive group J, and

(ii) a B block precursor which is the B block containing at least two reactive groups K, which may be the same or different, which will react with the reactive group J to form a link which is part of the polymer backbone,

the molar ratio of (i) to (ii) being at least 2, thus making a TPE of the ABA, A_(n) B or (AB)_(n) type; or

II. reacting together

(i) a B block precursor which is the B block containing at least two reactive groups L, which may be the same or different, and

(ii) (a) a monomeric component comprising at least one monomer which will react with the group L and with itself or with a reactive group resulting from reaction of the monomeric component with the B block precursor, optionally with the aid of an initiator, to form the A block, or

(b) an A block precursor which is the A block containing at least one reactive group M which will react with the group L to form the A block; or

III. reacting together

(i) an A block precursor which is the A block terminated by a reactive group N, and

(ii) a monomeric component comprising at least one monomer which will react with the group N and with itself to form the B block with at least two A blocks pendant from the polymeric backbone of the soft block; or

IV. performing a living polymerization in which the monomers for the A and B blocks are polymerized separately and sequentially, using an initiator so that the growing polymer chain has a terminal group which reacts with the monomer present at that time and in turn produces a reactive terminal group on the residue of the monomer which has reacted with the growing polymer chain.

In all of these reactions, other ingredients may be present in order to modify the properties of the product, for example initiators, chain transfer agents and monomers which may be chemically or physically incorporated into the resulting TPE.

Third Aspect--Compositions, Shaped Articles and Assemblies Comprising the Novel TPE's

In a third aspect, this invention provides a composition, shaped article or assembly which comprises a novel TPE as defined above and a second component which is mixed with the TPE, or which is surrounded (e.g. encapsulated) by the TPE, or which contacts (e.g. surrounds or otherwise provides a substrate for) the TPE.

In one embodiment, this aspect of the invention is particularly valuable when the second component is a thermally responsive substance which undergoes a thermally induced change at a temperature T_(crit) which is above the temperature at which the TPE can conveniently be melt processed. Because the novel TPE's can be melt-processed at temperatures close to T_(q), generally below (T_(q) +60)°C., often below (T_(q) +40)°C., and even lower, they are superior to conventional TPE's which are usually melt processed at temperatures well above their melting point. Tact is preferably above (T_(q) +10)°C., e.g. (T_(q) +10)°C. to (T_(q) +40)°C. or (T_(q) +60)°C.

In another embodiment, this aspect of the invention is particularly valuable when the second component is intimately mixed with the TPE and is a crystalline polymeric additive, preferably an SCC polymer, which

(a) has a first order transition point Ta in the composition of 23° to 120° C., preferably 30° to 60° C., and

(b) has a heat of fusion of at least 5 Joules/g, preferably at least 20 Joules/g.

The presence of the crystalline additive can substantially improve the shear value of the composition. This is particularly useful when the composition is to be used as a PSA, for which purpose the composition may also contain an amorphous polymer, e.g. a conventional PSA, as well as other conventional ingredients of PSA's.

Fourth Aspect--Making Shaped Articles of the Third Aspect of the Invention

In a fourth aspect, this invention provides a process for making a shaped article, which process comprises

(A) melting a novel TPE as defined above,

(B) dispersing an additive in the molten TPE,

(C) shaping the dispersion from step B, and

(D) cooling the shaped article from step C to a temperature below T_(q).

Fifth Aspect--Releasing Second Components from Compositions, Shaped Articles and Assemblies of the Third Aspect of the Invention

In a fifth aspect, this invention provides a process for releasing the second component from a composition, shaped article or assembly of the third aspect of the invention, which process comprises heating the composition, article or assembly by means of heat which is (i) generated by a mammalian body or (ii) generated artifically, e.g. by an electrical or other heater or by an engine or electrical motor, and/or (iii) conveyed artifically to the TPE. The heat may be conveyed to the TPE by convection, conduction or radiation, but is preferably conveyed by means of a stream of heated fluid, e.g. heated air or a body fluid, which also assists in removal of the second component from the TPE.

Sixth Aspect--PSA's and PSA Composites Comprising TPE's Containing SCC Blocks, and Methods of Using Them

In a sixth aspect, this invention provides a composition which is suitable for use as (or in the production of) a pressure-sensitive adhesive (PSA) and which comprises a TPE in which the A blocks, or the B blocks, or both, are SCC blocks. Particularly useful PSA compositions comprise a mixture of the TPE with (a) a crystalline polymer additive, preferably a side chain crystallizable (SCC) polymer, and/or (b) with an amorphous polymer (which may be an elastomer), e.g. a known PSA. In this aspect, the invention includes also PSA composites comprising a backing having a coating thereon of such a composition, particularly PSA-coated articles for use in the medical field, for example an assembly which comprises

(i) a flexible backing,

(ii) a solvent-free layer of a pressure-sensitive adhesive (PSA) which is secured to the backing, and which comprises a TPE or is at least partially covered by a layer comprising a TPE, said TPE comprising polymeric molecules which comprise

(i) polymeric A blocks which

(a) are crystalline and have a melting point T_(q), or

(b) are amorphous and have a glass transition point T_(gh) ;

(ii) at least one polymeric B block which is linked to at least two A blocks and which

(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C. or

(b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C.

wherein at least one block selected from the A and B blocks comprises a side chain comprising crystallizable moieties which render the block crystalline. This aspect of the invention also includes processes for preparing assemblies by joining articles together using such a composition; and processes for disassembling such assemblies which include heating the PSA to weaken it. These PSA's, PSA composites, assemblies, and processes preferably have the functional characteristics set out in the Schmitt et al applications incorporated by reference herein, which also discloses amorphous base resins, crystalline polymer additives, methods of formulating PSA's, methods of applying PSA's to backings, backings, and methods of using PSA composites, which are generally suitable for use in this aspect of the invention.

Seventh Aspect--Heat-Sealed Assemblies Comprising Articles Comprising TPE's Containing SCC Blocks

In a seventh aspect, this invention provides a film or other article which comprises a TPE in which the A blocks, or the B blocks, or both, are SCC blocks, particularly an article which is suitable for use as a component of a food package and/or in a method which requires heat-sealing the film These films preferably have the functional characteristics set out in Stewart Ser. No. 07/885,915 incorporated by reference herein, which also discloses food packages, and methods of packaging and storing foodstuffs, suitable for use in this aspect of the invention. One assembly according to this aspect of the invention comprises

(1) a first film which comprises a TPE comprising polymeric molecules which comprise

(i) polymeric A blocks which

(a) are crystalline and have a melting point T_(q), or

(b) are amorphous and have a glass transition point T_(gh) ;

(ii) at least one polymeric B block which is linked to at least two A blocks and which

(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C. or

(b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C.

wherein at least one block selected from the A and B blocks comprises a side chain comprising crystallizable moieties which render the block crystalline, and

(2) a second film which is heat-sealed to the first film and which is composed of a polymeric composition which is compatible with the A block or the B block or both.

Eighth Aspect--Hot Melt Adhesives Comprising TPE's Containing SCC Blocks

In an eighth aspect, this invention provides a hot melt adhesive comprising a TPE in which the A blocks, or the B blocks, or both, are SCC blocks and processes for joining two articles together which comprise forming a layer of a molten polymeric composition containing such a TPE between the articles, pushing the articles together, and allowing the composition to cool. Preferably the composition comprises a TPE comprising polymeric molecules which comprise

(i) polymeric A blocks which

(a) are crystalline and have a melting point T_(q), or

(b) are amorphous and have a glass transition point T_(gh) ; and

(ii) at least one polymeric B block which is linked to. at least two A blocks and which

(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C. or

(b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C.

wherein at least one block selected from the A and B blocks comprises a side chain comprising crystallizable moieties which render the block crystalline; and at least one of the articles to be joined is composed of a polymeric material which is compatible with the A block or the B block or both.

Ninth Aspect--PSA's, PSA Composites, and Methods of Using Them Disclosed in Schmitt et al Application Ser. Nos. 654,723, 829,494 and 928,800

In a ninth aspect, this invention provides PSA's, PSA composites, and methods of using them which are disclosed in the Schmitt et al Application Ser. Nos. 654,723 now abandoned, 829,494 now scheduled and 928,800 now U.S. Pat. No. 5,412,035 incorporated by reference herein.

A first embodiment of this ninth aspect of the invention is a pressure-sensitive adhesive composition which comprises

(1) a base resin, and

(2) a crystalline additive having a first order transition point T_(a) in the composition;

said composition, when tested for peel strength under selected test conditions as a PSA composite consisting of a selected backing and a layer of the PSA composition of selected thickness,

(i) at a selected temperature T₁ which is less than T_(a), having a PSA peel strength P₁ or undergoing non-adhesive failure, and

(ii) at a selected temperature T₂ which is higher than T_(a), having a PSA peel strength P₂ ;

a comparative composition which is the same as said composition except that it does not contain the additive, when tested for peel strength under the same test conditions, as a comparative PSA composite consisting of the same backing and a layer of the comparative PSA composition of the same thickness,

(i) at T₁, having a PSA peel strength P₁ ^(c) or undergoing non-adhesive failure, and

(ii) at T₂, having a PSA peel strength P₂ ^(c) or undergoing non-adhesive failure;

and at least one of the following conditions being fulfilled

(a) P₁ -P₂ is at least 25 g/cm,

(b) 100(P₁ -P₂)/P₁ is at least 25,

(c) the PSA composite undergoes non-adhesive failure at T₁,

(d) the comparative PSA composite undergoes non-adhesive failure at T₁ or T₂, and

(e) (P₁ -P₂)/P₁ is greater than (P₁ ^(c) -P₂ ^(c))/P₁ ^(c).

A second embodiment of this ninth aspect of the invention is a PSA composite which comprises

(A) a flexible backing, and

(B) a solvent-free layer of a pressure-sensitive adhesive composition which comprises

(1) a base resin, and

(2) a crystalline additive having a first order transition temperature T_(a) ;

said PSA composite, when tested for peel strength under selected test conditions,

(i) at a selected temperature T₁ which is less than T_(a), having a PSA peel strength P₁ or undergoing non-adhesive failure, and

(ii) at a selected temperature T₂ which is higher than T_(a), having a PSA peel strength P₂ ;

a comparative PSA composite, which is the same as said composite except that the pressure-sensitive adhesive does not contain the additive,

(i) at T₁, having a PSA peel strength P₁ ^(c) or undergoing non-adhesive failure, and

(ii) at T₂, having a PSA peel strength P₂ ^(c) or undergoing non-adhesive failure;

and at least one of the following conditions being fulfilled

(a) P₁ -P₂ is at least 25 g/cm,

(b) 100(P₁ -P₂)/P₁ is at least 25,

(c) the PSA composite undergoes non-adhesive failure at T₁,

(d) the comparative PSA composite undergoes non-adhesive failure at T₁ or T₂, and

(e) (P₁ -P₂)/P₁ is greater than (p₁ ^(c) -P₂ ^(c))/P₁ ^(c).

A third embodiment of this ninth aspect of the invention is an assembly which comprises a receptor and a PSA composite which is adherent to the receptor and which comprises

(A) a flexible backing, and

(B) between the backing and the receptor, a layer of a pressure-sensitive adhesive composition which comprises

(1) a base resin, and

(2) a crystalline additive having a first order transition temperature T_(a) in the composition;

said PSA composite, when tested for peel strength from said receptor under selected test conditions,

(i) at a selected temperature T₁ which is less than T_(a), having a PSA peel strength P₁ or undergoing non-adhesive failure, and

(ii) at a selected temperature T₂ which is higher than T_(a), having a PSA peel strength P₂ ;

and at least one of the following conditions being fulfilled

(a) P₁ -P₂ is at least 25 g/cm,

(b) 100(P₁ -P₂)/P₁ is at least 25, and

(c) the PSA composite undergoes non-adhesive failure at T₁.

A fourth embodiment of this ninth aspect of the invention is a process for removing a PSA composite from a receptor to which it is adhered, the PSA composite comprising

(A) a backing, and

(B) between and in contact with the backing and the receptor, a layer of a pressure-sensitive adhesive composition which comprises

(1) a base resin, and

(2) a crystalline additive having a first order transition temperature T_(a) in the composition,

which process comprises reducing the PSA peel strength of the PSA composite by heating the PSA composite from a temperature below T_(a) to a temperature above T_(a), and removing the PSA composite from the receptor while the PSA composite is at a temperature above T_(a).

A fifth embodiment of the ninth aspect of this invention is a pressure-sensitive adhesive (PSA) composition which comprises

(a) at least 50% by weight of a base resin which is a PSA, and

(b) up to 50% by weight of a side-chain crystallizable polymer which has a heat of fusion of at least about 20 J/g and which comprises recurring units having the structural formula ##STR1## wherein W and X are each respectively a first and a second monomer unit, which monomer unit may be any molecular moiety connectable to an adjoining molecular moiety, Y and Z are each independently a backbone monomer unit which may be any molecular moiety or atom, each S is independently a linking group or spacer unit and is optionally present, Cyt and Cy are each independently a crystallizable moiety connected to the respective backbone, and a, b, c and d are each, independently, integers ranging from 0 to 1,000 with the proviso that sufficient Cyt and Cy are present so as to provide a molecular weight which is equal to or greater than twice the sum of the molecular weights of W, X, Y and Z.

Tenth Aspect--Packages and Novel Copolymers Disclosed in Stewart Application Ser. Nos. 885,915 and 623,602

In a tenth aspect, this invention provides packages and novel copolymers which are disclosed in the Stewart Application Ser. Nos. 885,915 and 623,602 incorporated by reference herein.

A first embodiment of this tenth aspect of the invention is a package which is surrounded by air and which comprises

(1) a container which retains its shape at temperatures between 0° C. and 40° C., and

(2) within the container, a biological material which is actively respiring and which is selected from the group consisting of foods and flowers;

said container comprising one or more control sections which provide the only way in which oxygen, carbon dioxide and water vapor from the air can enter or leave the container, at least one of said control sections being a first control section composed of a polymeric material which

(a) comprises a crystalline polymer having a first order transition point T_(m) from 0° to 40° C. and a heat of fusion of at least 5 J/g, and

(b) is sufficiently permeable to oxygen, carbon dioxide and water vapor, and exhibits an increase in permeability to at least one of oxygen and carbon dioxide which increases by a factor at least 2.5 over a temperature range of 10° C. between 0° C. and 40° C., such that said one or more control sections cause said package to provide an environment around the biological material which adjusts to the respiration of the biological material so as to extend its shelf life when the temperature of the container and the biological material changes within the temperature range of 0° to 40° C.

A second embodiment of this tenth aspect of the invention is a method of storing a biological material which is actively respiring and which is selected from the group consisting of foods and flowers, which method comprises

(A) placing the biological material inside a container which

(1) retains its shape at temperatures between 0° and 40° C.,

(2) comprises one or more control sections which provide the only way in which oxygen, carbon dioxide and water vapor can enter or leave the container, at least one of said control sections being a first control section composed of a polymeric material which

(a) comprises a crystalline polymer having a first order transition point T_(m) from 0° to 40° C. and a heat of fusion of at least 5 J/g, and

(b) is sufficiently permeable to oxygen, carbon dioxide and water vapor, and exhibits an increase in permeability to at least one of oxygen and carbon dioxide which increases by a factor at least 2.5 over a temperature range of 10° C. between 0° C. and 40° C., such that said one or more control sections cause said package to provide an environment around the biological material which adjusts to the respiration of the biological material so as to extend its shelf life when the temperature of the container and the biological material changes within the temperature range of 0° to 40° C.

(B) storing the container in air, with the biological material inside it, at a first temperature T₁ which is at least 0° C. and less than 40° C.; and

(C) storing the container in air, with the biological material inside it, at a second temperature T₂ which is above T₁ and at most 40° C. and at which the permeability of the first control section to at least one of oxygen and carbon dioxide is at least 2.5 times the permeability at T₁.

A third embodiment of this tenth aspect of the invention is a copolymer which is novel, which has a heat of fusion of at least 5 J/g, and which has the structural formula ##STR2## wherein W and X are each respectively a first and a second monomer unit, which monomer unit may be any molecular moiety connectable to an adjoining molecular moiety (i.e., polymerizable), Y and Z are each independently a backbone monomer unit which may be any molecular moiety or atom, each S is independently a linking group or spacer unit and is optionally present, Cyt and Cy are each independently a crystallizable moiety connected to the respective backbone directly or via the spacer unit, and a, b, c, d and e are each, independently, integers ranging from 0-1,000 with the proviso that sufficient Cyt and Cy are present so as to provide a Mw which is equal to or greater than twice the sum of the Mws of W, X, Y and Z.

A fourth embodiment of this tenth aspect of the invention is an assembly which comprises

(i) a first polymeric film, and

(ii) a second polymeric film which is heat sealed to the first film and which comprises a copolymer as just defined.

A fifth embodiment of this tenth aspect of the invention is a package which comprises a foodstuff or biological material which is actively respiring and a container therefor, at least a part of said container being composed of a block copolymer of a side-chain crystallizable polymer and a second polymer which exhibits a glass transition or melting point higher than the side-chain crystallizable polymer.

Eleventh Aspect--Methods and Apparatus Disclosed in Schmitt Application Ser. No. 939,110

In an eleventh aspect, this invention provides methods and apparatus which are disclosed in the Schmitt Application Ser. No. 939,110 incorporated by reference herein.

A first embodiment of this eleventh aspect of the invention is a method of occluding a channel in a living mammal, comprising the steps of:

heating a polymer or composite to a temperature such that the polymer or composite is flowable;

injecting the flowable polymer or composite into the channel; and

allowing the polymer or composite to cool and become non-flowable in the channel.

A second embodiment of this eleventh aspect of this invention is a channel-occluding unit, comprising:

an injecting device; and

a polymeric material or composite in the injecting device, the polymeric material being injectable from the device and having a melting point below 50° C. and a freezing point above 30° C.

A third embodiment of this eleventh aspect of the invention is a method for removing an occluder from a channel in a living mammal, the occluder comprising solidified polymer having a melting point

(i) sufficiently high that the polymer is non-flowable when at the temperature of the channel, and

(ii) sufficiently low that melted polymer can be injected into the channel without damaging the mammal, the method comprising the step of heating the occluder to melt the polymer.

BRIEF DESCRIPTION OF THE DRAWING

This invention is illustrated in the accompanying drawing, in which FIG. 1 illustrates, partly in cross-section, a PSA composite of the invention, comprising a backing 1; a layer of a novel PSA adhesive 2 which is in the form of a border and surrounds a sterilized wound dressing 3, and a receptor 5, e.g. human skin; and FIG. 2 is a cross-section through a PSA composite of the invention comprising a backing 1, a layer 4 of conventional PSA, a layer 2 of a PSA of the invention, and a release sheet 6.

DETAILED DESCRIPTION OF THE INVENTION

For clarity and convenience, the following detailed description of the invention is divided into various headings and sub-headings, e.g. by reference to the various different aspects of the invention. It is to be understood, however, that where a particular feature is discussed only under one heading, e.g. in relation to one aspect of the invention, that feature is applicable to the invention generally, and can for example be used in other aspects of the invention.

DEFINITIONS, ABBREVIATIONS AND MEASUREMENTS

In this specification, unless otherwise stated, parts, amounts and percentages are by weight. Temperatures are in °C. Molecular weights are in Daltons and are determined by gel permeation chromatography (GPC) in THF (tetrahydrofuran) against a polystyrene standard, the M_(n) values being number average molecular weights and the M_(w) values being weight average molecular weights. In some places, M_(w) values are given in thousands, abbreviated as "k"; thus an M_(w) given as 65 k means that the weight average molecular weight is 65,000 Daltons. First order transition points (often referred to as melting points), glass transition points, and heats of fusion are determined by a differential scanning calorimeter (DSC), using the second heat cycle and a heating rate of 10° C./minute. The peak of the DSC curve is T_(q) when the measurement is carried out on the TPE, and T_(m) when the measurement is carried out on the hard block precursor before it is incorporated into the TPE. Glass transition points are taken at the mid-point (first derivative) of the secondary transition. Elongation (El) and tensile strength (TS) values are measured at 25° C. using a tensile test instrument, for example an Instron tensile tester, at a crosshead speed of 0.5 inch/minute (1.27 cm/minute). Modulus values are Young's Modulus (YM) values measured in the same way as the elongation values. Viscosity values are measured at 25° C. and a solids content of 30% (we used a Brookfield Viscometer Model LVT) and expressed in centipoise. Complex viscosity and complex modulus values are measured at a rate of 0.05 radians/second, unless otherwise specified (we used a Rheometrics cone-and-plate mechanical spectrometer). The recrystallization time (XL time) is measured by a procedure in which (a) a steel plate having on its top surface a layer 10 microns thick of the TPE is heated to 60° C., (b) the plate is placed on a cooling surface maintained at 25° C., and (c) a glass rod, 0.2 cm in diameter, is dipped into the TPE at frequent intervals; the recrystallization time is the time elapsed between placing the plate on the cooling surface and the time when it is no longer possible to draw a fine string of TPE from the plate with the glass rod.

The term Cn is used herein to denote a linear compound or group containing n carbon atoms, and the abbreviations CnA, CnMA and CnIEMA are used to denote linear alkyl acrylates, linear alkyl methacrylates, and linear alkyl oxycarbonylamido-ethylmethacrylates in which the alkyl group contain n carbon atoms. For example, C4A is butyl acrylate, C16A is hexadecyl acrylate, and C22MA is docosanyl (also known as behenyl) methacrylate. The abbreviations EHA, HEA, MBA and AA are used for 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, 3-methoxybutyl acrylate, and acrylic acid, respectively. The abbreviation AIBN is used for azo bis-isobutyronitrile. The abbreviation IEMA is used for isocyanatoethylmethacrylate.

Shear and Tack Values are measured by Test Procedures PSTC-7 and PSTC-6, respectively, of the Pressure-Sensitive Tape Council. In the Shear Test, a sample of the PSA composite 0.5 inch (1.25 cm) square is pressed against a vertical steel plate, and after 5 minutes, a 1000 g weight is secured to the backing; the shear value is the time in seconds before the backing falls off the plate. In the Tack Test, a ball bearing 7/16 inch (1.1 cm) in diameter is allowed to roll down a standard incline onto the PSA surface of the composite; the tack value is the distance in cms that the ball runs over the PSA.

Peel Strengths for PSA composites applied to human skin are measured as follows. After removing the release sheet (if any), two identical samples are placed on the underside of the forearm of an adult, with the length of the strips parallel to the arm bone. Light hand pressure is applied to the entire surface of the strips. After about 0.5 hour, 1 hour, 24 hours, or 48 hours, one end of one strip is detached from the skin and attached to a clip which is attached by a wire to the load cell of an Instron Materials Testing Instrument (IMTI) or an equivalent instrument. The sample is then removed by peeling it off at a rate of 10 inch (25.4 cm) per minute, the sample being bent back over itself at an angle of about 180°. The other strip is removed in the same way, except that a hair dryer is used to warm the entire strip to a temperature of about 40° C. before it is peeled off. The average peel strength for each strip is recorded at room temperature (LT) and at the higher temperature (HT).

Moisture Vapor Transmission Rates (MVTR) are measured by ASTM E96-60, using the desicant method, at 37° C. and a humidity difference of about 70%, and are expressed in g/mil/m² /24 hr.

SCC BLOCKS

The crystallizable moieties in the side chains of the SCC blocks are preferably such that a DSC scan of the TPE shows a very sharp melting point which results from melting of the crystallizable moieties, for example a difference between the onset of melting (T_(o)) and the peak (T_(q) or T_(ms)) on a DSC curve of less than 10° C., preferably less than 8° C., particularly less than 6° C., especially less than 4° C. The melting point of the SCC block on its own, i.e. of the block precursor or of an equivalent polymer, which is referred to herein as T_(m), is closely related to T_(q).(in a hard block) or T_(ms) (in a soft block). T_(q) or T_(ms) will generally be between (T_(m) -10)°C. and (T_(m) +5)°C., usually between (T_(m) -5)°C. and T_(m). T_(q) and/or T_(ms) are selected according to the intended use of the TPE and are generally 0° to 200° C., preferably less than 150° C., particularly less than 85° C. In the SCC blocks, preferably 50 to 100%, particularly 70 to 100%, especially 90 to 100%, of the repeating units contain crystallizable side chains. The crystallizable side chains may be the same or different. The heat of fusion of the SCC block on its own is generally at least 5 or at least 10, preferably at least 20, particularly at least 40, for example 60 to 120, Joules/g. The heat of fusion of the SCC block in the TPE will depend upon the heat of fusion of the SCC block on its own and upon the weight proportion of the SCC block in the TPE. Thus if the TPE contain p% of an SCC block, the heat of fusion of that SCC block in the TPE will generally be about 0.01 p times the heat of fusion of the SCC block on its own, or less.

Known SCC's which can form SCC blocks in the TPE's used in this invention include polymers of one or more monomers such as substituted and unsubstituted acrylates, fluoroacrylates, vinyl esters, acrylamides, maleimides, α-olefins, p-alkyl styrenes, alkylvinyl ethers, alkylethylene oxides, alkyl phosphazenes and amino acids; polyisocyanates; polyurethanes; polysilanes; polysiloxanes; and polyethers; all of such polymers containing long chain crystallizable groups. Suitable SCC's are described for example in J. Poly. Sci. 60, 19 (1962), J. Poly. Sci, (Polymer Chemistry) 7, 3053 (1969), 9, 1835, 3349, 3351, 3367, 10, 1657, 3347, 18, 2197, 19, 1871, J. Poly. Sci, Poly-Physics Ed 18 2197 (1980), J. Poly. Sci, Macromol. Rev, 18, 117 (1974), Macromolecules 12 ,94 (1979), 13, 12, 15, 18, 2141, 19, 611, JACS 75, 3326 (1953), 76; 6280, Polymer J 17, 991 (1985); and Poly. Sci USSR 21, 241 (1979).

The SCC blocks in the TPE's used in this invention can be broadly defined as polymer blocks which comprise repeating units of the general formula ##STR3## where Y is an organic radical forming part of the polymer backbone and Cy comprises a crystallizable moiety. The crystallizable moiety may be connected to the polymer backbone directly or through a divalent organic or inorganic radical, e.g. an ester, carbonyl, amide, hydrocarbon (for example phenylene), amino, or ether link, or through an ionic salt linkage (for example a carboxyalkyl ammonium, sulfonium or phosphonium ion pair). The radical Cy may be aliphatic or aromatic, for example alkyl of at least 10 carbons, fluoralkyl of at least 6 carbons or p-alkyl styrene wherein the alkyl contains 6 to 24 carbons. The SCC block may contain two or more different repeating units of this general formula. The SCC may also contain other repeating units, but the amount of such other units is preferably such that the total weight of the crystallizable moieties is at least twice the weight of the remainder of the block.

Preferred SCC blocks comprise side chains containing in total at least 5 times as many carbon atoms as the backbone of the block, particularly side chains comprising linear polymethylene moieties containing 12 to 50, especially 14 to 22, carbon atoms, or linear perfluorinated or substantially perfluorinated polymethylene moieties containing 6 to 50 carbon atoms. Blocks containing such side chains can be prepared by polymerizing one or more corresponding linear aliphatic acrylates or methacrylates, or equivalent monomers such as acrylamides or methacrylamides. A number of such monomers are available commercially, either as individual monomers or as mixtures of identified monomers, for example C12A, C14A, C18A, C22A, a mixture of C18A, C20A and C22A, a mixture of C26A to C40A, fluorinated C8A (AE800 from American Hoechst) and a mixture of fluorinated C8A, C10A and C12A (AE12 from American Hoechst). The blocks can optionally also contain units derived from one or more other comonomers preferably selected from other alkyl, hydroxyalkyl and alkoxyalkyl acrylates, methacrylates (e.g. glycidal methacrylate), acrylamides and methacrylamides; acrylic and methacrylic acids; acrylamide; methacrylamide; maleic anhydride; and comonomers containing amine groups. Such other co-monomers are generally present in total amount less than 50%, particularly less than 35%, especially less than 25%, e.g. 0 to 15%. They may be added to modify the melting point or other physical properties of the TPE. The melting point of a block containing such polymethylene side chains is influenced by the number of carbon atoms in the crystallizable side chains. For example, homopolymers of C14A, C16A, C18A, C20A, C22A, C30A, C40A and C50A respectively typically have melting points of 20°, 36°, 49°, 60°, 71°, 76°, 96° and 102° C., while the homopolymers of the corresponding n-alkyl methacrylates typically have melting points of 10°, 26°, 39°, 50°, 62°, 68°, 91° and 95° C. Copolymers of such monomers generally have intermediate melting points. Copolymers with other monomers, e.g. acrylic acid or butyl acrylate, typically have somewhat lower melting points.

Other polymers which can be used for precursors of SCC blocks in TPE's used in this invention, or which can be formed by a living polymerization on another preformed block, include atactic and isotactic polymers of n-alkyl α-olefins (e.g. the atactic and isotactic polymers of C₁₆ olefin, having T_(m) 's of 30° and 60° C. respectively); polymers of n-alkylglycidyl ethers (e.g. the polymer of C₁₈ alkyl glycidylether); polymers of n-alkyl vinyl ethers (e.g. the polymer of C₁₈ alkylvinylether having a T_(m) of 55° C.); polymers of n-alkyl-α-epoxides (e.g. the polymer of the C₁₈ alkyl α-epoxide having a T_(m) of 60° C.); polymers of n-alkyl oxycarbonylamidoethylmethacrylates (e.g. the polymers of C18 IEMA, C22 IEMA and C30 IEMA having T_(m) 's of 56°, 75° and 79° respectively); polymers of n-fluoro alkyl acrylates (e.g. the polymers of C₈ hexadecafluoroalkylacrylate, and of a mixture of C₈₋₁₂ alkyl fluoroacrylates having T_(m) 's of 74° and 88° C. respectively), polymers of n-alkyloxazolines (e.g. the polymer of C₁₆ alkyl oxazoline having a T_(m) of 155° C.); polymers obtained by reacting an hydroxyalkyl acrylate or methacrylate with an alkyl isocyanate (e.g. the polymers obtained by reacting hydroxyethyl acrylate with C₁₈ or C₂₂ alkyl isocyanate and having T_(m) 's of 78° and 85° respectively); and polymers obtained by reacting a difunctional isocyanate, a hydroxyalkyl acrylate or methacrylate, and a primary fatty alcohol (e.g. the polymers obtained by reacting hexamethylene diisocyanate, 2-hydroxyethyl acrylate, and C₁₈ or C₂₂ alcohols, and having T_(m) 's of 103° and 106° C. respectively).

Preferred SCC blocks in the TPE's used in this invention comprise 60 to 100% of units derived from at least one monomer selected from the group consisting of alkyl acrylates, alkyl methacrylates, N-alkyl acrylamides, N-alkyl methacrylamides, alkyl oxazolines, alkyl vinyl ethers, alkyl vinyl esters, α-olefins, alkyl 1,2-epoxides and alkyl glycidyl ethers in which the alkyl groups are n-alkyl groups containing 14 to 50 carbon atoms, and the corresponding fluoroalkyl monomers in which the alkyl groups are n-alkyl groups containing 6 to 50 carbon atoms; 0 to 20% of units derived from at least one monomer selected from the group consisting of alkyl acrylates, alkyl methacrylates, N-alkyl acrylamides, alkyl vinyl ethers, and alkyl vinyl esters in which the alkyl groups are n-alkyl groups containing 4 to 12 carbon atoms; and 0 to 15% of units derived from at least one polar monomer selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, acrylamide, methacrylamide, acrylonitrile, methacrylonitrile, vinyl acetate and N vinyl pyrrolidone. Such SCC block polymers may also contain units derived from other monomers to change compatibility with other blocks, or to raise the modulus of the TPE; such monomers include styrene, vinyl acetate, monoacrylic functional polystyrene and the like.

The number average molecular weight of the SCC block is preferably less than 200,000, more preferably less than 100,000, particularly less than 50,000, more particularly 2,000 to 20,000, especially 3,000 to 20,000.

A particular advantage of the present invention is that the molecular weight of the SCC block can be adjusted (for example through choice of the reaction conditions and addition of chain transfer agents) so as to optimize the mechanical properties of the TPE without substantial change in T_(q) or T_(ms).

SCC HARD (A) BLOCKS

When a TPE used in this invention includes hard SCC blocks, preferably all the hard blocks in the TPE are SCC blocks. The hard SCC blocks are preferably all of the same type, with each block being derived from the same monomer or mixture of monomers. When two different SCC hard blocks are present, the TPE may have two or more distinct T_(q) 's, corresponding to the different SCC blocks. When conventional hard blocks are also present, they preferably do not amount to more than 10%, particularly not more than 5%, of the TPE. Such other hard blocks, if present, can be of any kind, including those disclosed in the documents incorporated by reference herein.

As indicated above, T_(q) will be selected according to the intended use of the TPE. When the TPE is used in a human or other animal, T_(q) is selected so that the TPE is solid at normal temperatures but molten at an elevated temperature which can be tolerated by the animal. For such use, T_(q) is preferably 30° to 50° C., particularly 34° to 45° C., more particularly 37° to 44° C., e.g. 40° to 44° C. when the TPE is to be used in humans. When the TPE is associated with an explosive propellant, or other energetic material, T_(q) is preferably 60° to 110° C., particularly 75° to 105° C. When the TPE is associated with a pharmaceutical, T_(q) is generally 10° to 80° C., preferably 25° to 50° C.

NON-SCC SOFT (B) BLOCKS

The non-SCC soft (B) blocks in the novel TPE's of the invention can be of any kind, including those disclosed in the documents incorporated by reference herein. The TPE can contain one or more different types of non-SCC B blocks. The glass transition point (T_(gs)) or melting point (T_(ms)) of the B blocks should be below (T_(q) -10)°C., preferably less than (T_(q) -20)°C., particularly less than (T_(q) -40)°C. T_(gs) or T_(ms) should also be below the temperature at which the TPE should exhibit elastomeric properties in use, for example less than 20° C., preferably less than 0° C., particularly less than -20° C., e.g. less than -40° C.

When the TPE contains more than one non-SCC B block, the B blocks will usually be the same; however, the TPE can contain two or more different B blocks. A B block can contain a single repeating unit (which may be derived from a single monomer or a pair of monomers) or two or more different repeating units. When there are two or more different repeating units in a B block, they can be distributed randomly or in blocks.

Examples of suitable amorphous B blocks are polyethers (containing, for example, between the ether linkages, an aliphatic, aromatic or mixed aliphatic aromatic group, and derived for example from tetrahydrofuran); polyacrylates (this term being used to include polymers of at least one alkyl acrylate, methacrylate, acrylamide or methacrylamide, optionally with other copolymerizable monomers such as acrylic acid, methacrylic acid, acrylamide, methacrylamide, acrylonitrile, acrolein, vinyl esters and styrene); polyesters (derived for example from a dihydroxy compound and a dicarboxylic acid or derivative thereof such as an acid chloride or ester); polyamides (derived for example from a lactone or from a diamine and a dicarboxylic acid or derivative thereof such as an acid chloride); polyurethanes (derived for example from a diisocyanate and a dihydroxy compound or a diamine); and polysiloxanes.

The linkages between repeating units in a B block can be the same as, or different from, the linkages between repeating units in the SCC A blocks. The linkages between the B block(s) and the A blocks can be the same as, or different from, the linkages between repeating units in the B block(s). They can for example be the residue of a linking compound which contains at least two reactive groups which will react with groups on the A and B blocks, for example a diisocyanate such as methylene diphenylene diisocyanate, tolylene diisocyanate, or hexamethylene diisocyanate.

The number average molecular weight of the B blocks is generally more than 5,000 and less than 900,000, preferably less than 500,000, particularly less than 200,000, especially less than 100,000, e.g. 10,000 to 80,000.

SCC SOFT (B) BLOCKS

When a TPE used in this invention includes soft SCC blocks, preferably all the soft blocks in the TPE are SCC blocks. The soft SCC blocks are preferably all of the same type, with each block being derived from the same monomer or mixture of monomers. When two different SCC soft blocks are present, the TPE may have two or more distinct T_(ms) 's, corresponding to the different SCC blocks. When conventional soft blocks are also present, they preferably do not amount to more than 10%, particularly not more than 5%, of the TPE. Such other soft blocks, if present, can be of any kind, including those disclosed in the documents incorporated by reference herein.

As indicated above, T_(ms) will be selected according to the intended use of the TPE. Thus T_(ms) can be selected so that the TPE changes, over a predetermined and relatively narrow temperature range including T_(ms), between a relatively hard and inflexible material and an elastomeric material. For most uses, T_(ms) is preferably less than 60° C., particularly less than 45° C., especially less than 30° C. T_(ms) is also preferably more than 0° C., particularly more than 5° C. For example, T_(ms) may be 3° to 40° C., preferably 5° to 20° C. In one preferred embodiment, the B block is a polyacrylate, preferably a polyacrylate which contains 50 to 100%, preferably 80 to 100%, of units derived from at least one n-alkyl acrylate or methacrylate in which the alkyl group contains 4 to 16, particularly 12 to 14, carbon atoms or from an equivalent monomer, e.g. an acrylamide or methacrylamide. Such B blocks may for example include units derived from one or more other ethylenically unsaturated comonomers including AA, EHA, HEA, MBA and methacrylic acid.

NON-SCC HARD (A) BLOCKS

When a TPE used in this invention includes non-SCC hard (A) blocks, the detailed description given above for non-SCC soft (B) blocks is equally applicable, subject only to the limitation that the melting point (T_(mh)) or glass transition point (T_(gh)) of the block must be higher, rather than lower, than the melting point of the SCC block (T_(ms)). Thus T_(ms) should be below (T_(mh) -10)° C. or (T_(gh) -10)°C., preferably below (T_(mh) -20)°C. or (T_(gh) -20)°C., particularly below (T_(mh) -40)°C. or (T_(gh) -40)°C.

NOVEL TPE's CONTAINING SCC HARD (A) BLOCKS

So that the novel TPE can show elastomeric properties, each soft (B) block must be linked to at least two SCC A blocks having a T_(q) higher than the T_(gs) or T_(ms) of the B block. The A blocks are insoluble in the B block(s) when the TPE is solid, and therefore anchor the B block(s) at temperatures below T_(q), thus providing elastomeric properties below T_(q) and above T_(gs), in a similar fashion as the A blocks in known TPE's. However the crystallizable side chains in the novel A blocks apparently plasticize the TPE at temperatures above T_(q) and thus assist in the very rapid reduction in viscosity at temperatures just above T_(q). The greater the compatibility of the A and B blocks above T_(q), the larger the reduction in viscosity. The complex viscosity of the TPE preferably decreases from a first value Q₁ dynes/cm² to a second value Q₂ dynes/cm², where Q₂ is less than Q₁ ×10⁻³, preferably less than Q₁ ×10⁻⁵, as the temperature increases from T₁ to T₂, where T₁ is less than T_(q), e.g. (T_(q) -3)°C., (T_(q) -5)°C. or (T_(q) -10)°C. and T₂ is at most (T_(q) +10)°C., e.g. (T_(q) +7)°C. or (T_(q) +4)°C. The TPE exhibits a corresponding decrease in complex modulus over the same temperature range.

When the soft block is crystalline, preferably T_(q) is 40° to 125° C. and T_(ms) is 3° to 40° C. In one preferred TPE, the B block comprises 50 to 100%, preferably 75 to 100%, by weight of units derivable from at least one n-alkyl acrylate or methacrylate in which the n-alkyl group contains 4 to 16 carbon atoms, preferably C12A or C14A or both, and the A block comprises 50 to 100%, preferably 75 to 100%, by weight of units derivable from at least one n-alkyl acrylate or methacrylate in which the n-alkyl group contains at least 18 carbon atoms, preferably 18-30 carbon atoms, particularly from C22A.

The novel TPE's generally have an ABA (triblock), (AB)_(n), or A_(n) B structure where n is at least 2, though mixtures of such structures can be used. The A_(n) B structure includes the various different types of graft copolymer which can be prepared. The novel TPE's will generally contain 2 to 90% of the SCC hard blocks. TPE's to be used in PSA's preferably contain 2 to 15%, particularly 3 to 10%, of the SCC hard blocks. TPE's for other uses can contain for example 10 to 90%, preferably 10 to 70%, particularly 25 to 60 , of the SCC hard blocks. The crystallizable moieties in the SCC hard blocks may provide less than 65%, particularly less than 60%, of the TPE.

The TPE's can be prepared by preparing separate precursor polymers corresponding to the A and B blocks, and then reacting the precursors, if necessary after functionalizing one or both of the precursors. For example an A block precursor containing at least one hydroxyl or amino group (e.g. a polymer prepared by polymerizing acrylic monomers and a capping agent or by polymerizing an alkyl epoxide or oxazoline) can be reacted with a B block precursor containing two or more isocyanate or acid chloride groups.

The TPE's can also be prepared by preparing a precursor polymer corresponding to the B block, and then polymerizing the monomer (or monomers) for the A block on the precursor, if necessary after functionalizing both ends of the precursor. For example, a B block precursor can be difunctionalized with mercapto groups, and the A blocks can then be prepared by adding an acrylic monomer and initiator to the difunctionalized precursor.

In another method, purified monomers are added to a reaction medium containing a suitable initiator in the order in which they are desired to add onto a living, growing polymer chain. For example a living cationic polymerization can be carried out by adding an SCC hard block monomer, followed by a soft block monomer, and either a hard block monomer to terminate the polymer chain or a series of hard and soft block monomers to prepare a block copolymer of desired composition. Such a method can make use of an HI/I₂ initiator system of the kind disclosed in Macromolecules 18 213 (1985).

The TPE's can also be prepared by preparing a precursor polymer corresponding to the A block, preferably an SCC acrylate or methacrylate polymer, and having a terminal unit which is copolymerizable with the monomer(s) for the soft block and then polymerizing the monomer(s) for the soft block, preferably an alkyl acrylate or methacrylate under conditions such that at least two A block precursor molecules are incorporated in the backbone of each polymer chain formed by the soft block monomer(s). For example an SCC acrylate polymer can be prepared, capped with mercapto ethanol, functionalized by reaction with isocyanatoethylmethacrylate, methacryloyl isocyanate, acryloyl chloride or methacryloyl chloride, and then reacted with butyl acrylate and/or a similar low molecular weight acrylate. The proportions of the reactants and the presence of a chain transfer agent can be used to control the ratio of soft blocks to hard blocks.

The TPE's used in this invention generally exhibit elongations of 5 to 500%, e.g. 50 to 500%. Their modulus is generally 10 to 100,000 psi (0.7 to 7,000 kg/cm²), e.g. 10 to 50,000 psi (0.7 to 3500 kg/cm²). The higher the proportion of hard blocks, the higher the modulus. The TPE's generally contain less than 90%, preferably less than 70%, and more than 2% of the hard blocks.

When a TPE containing crystalline A blocks is cooled from a temperature above T_(q) to a temperature substantially below T_(q), it does not recrystallize as soon as the temperature T_(q) is reached. There is a delay before recrystallization takes place. The recrystallization time (XL time) measured as described above is a measure of that delay, though it should be pointed out that the time to recrystallization is generally reduced as T_(q) increases above the measurement temperature. The length of the delay which is preferred varies from application to application. For example if the molten TPE (alone or with additives) is being introduced (e.g. extruded or injected) into a mold or channel, too short a recrystallization time may cause the TPE to solidify before it has filled the mold and/or in the apparatus used to introduce it, especially if a fine needle is used to inject the molten TPE. On the other hand, too long a recrystallization time may result in at least some of the molten TPE running out, or being washed out, of the channel or mold before it has solidified. One of the advantages of this invention is that by appropriate changes in the repeating units of the SCC hard block, and/or the ratio of hard blocks to soft blocks, the recrystallization time can be changed in a controllable way. The TPE's, when used to occlude a channel in a living mammal, preferably have recrystallization times of 5 to 150 seconds, preferably 10 to 97 seconds, particularly 10 to 73 seconds.

The number average molecular weight (M_(n)) of the TPE's used in this invention is generally 5,000 to 800,000, preferably 10,000 to 800,000, for example 5,000 to 400,000, particularly 10,000 to 200,000. The ratio M_(w) /M_(n) is generally from 1 to 15, e.g. 2 to 4.

COMPOSITIONS. SHAPED ARTICLES. AND ASSEMBLIES

In the compositions, shaped articles, and assemblies of the invention, a TPE containing SCC hard blocks is associated with a second component which contacts the TPE. The term "associated with" is used herein in a broad sense to include compositions in which the second component is a solid which is distributed, preferably uniformly, throughout the TPE; shaped articles in which the TPE surrounds, preferably encapsulates, the second component, which may be in the form of small particles; and assemblies in which the TPE is supported, e.g. at least partially surrounded, by the second component. The amount of the TPE in the composition is generally at least 10%, preferably at least 15%, and may be more, e.g. at least 20%, based on the weight of the TPE and the second component. The A block preferably has a solubility constant which ensures that second component is effectively wetted by the TPE in the molten state.

The invention is particularly useful when it is desired to make a solid composite containing a second component which is a thermally responsive material and which must be maintained below a relatively low critical temperature (T_(crit)) at least for storage purposes. Thus conventional TPE's are often unsatisfactory for this purpose because the thermally responsive material has a T_(crit) which is below the temperature at which the conventional TPE can conveniently be melt-processed. The novel TPE's, by contrast, can be melt-processed at much lower temperatures, and furthermore can be tailored to have a T_(q) appropriate to any value within a wide range of values for T_(crit). The value of T_(crit) can be set by reaction (including decomposition) of the second component.

Second components can be dispersed in the TPE by adding them slowly to the TPE while it is molten and at a temperature safely below T_(crit). The solid product obtained by shaping the molten composition (e.g. by extrusion or in a mold), followed by cooling, is mechanically tough and can absorb impact energy, thus reducing the danger of accidental explosion or the like. The product can also absorb thermal energy because significant heat will be absorbed in melting the hard blocks of the TPE. Furthermore, the product can be easily reheated and reprocessed if desired.

When the second component is dispersed in the TPE by melt mixing, and the amount of the additive is relatively high, e.g. greater than 50%, the composition may also contain a plasticizer to lower melt viscosity during the dispersion process. The plasticizer must be compatible with the TPE, but is preferably not compatible with the hard block so that its presence does not change the melting behavior of the TPE.

Particularly important active additives are the so-called "energetic" materials, including fuels, explosives, including low vulnerability explosives, rocket and gun propellants, munitions of all kinds, decoy flares, gas and smoke generators, and the various materials which may be mixed with them, including oxidizers, stabilizers, cure rate modifiers, burn rate modifiers, and plasticizers. Particular energetic materials are disclosed in U.S. Pat. Nos. 4,361,450 (Munson), 4,361,526 (Allen), 4,483,978 (Manser), 4,919,737 (Biddle et al) and 4,976,796 (Biddle et al), the disclosures of which are incorporated herein by reference. Current methods for making composites containing energetic materials make use of crosslinked elastomeric binders, which require complex heating schedules and which yield products which cannot be reprocessed.

Other thermally responsive second components include pharmacologically or biologically active materials (e.g. blood-coagulating compounds, spermicides, hormones, growth regulators and antibiotics), agricultural chemicals, seeds, catalysts and enzymes.

Other second components can provide the solid composition with desired properties such as toughness, elongation, thermal conductivity, opacity to radiation, e.g. X-rays, and good moisture vapor transmission. Such components include for example reinforcing fillers, including fibers, gold powder, silver powder, radio-opaque pigments, fumed silica, and hydrophilic materials such as carboxymethyl cellulose, guar gum, carragenan and cellulosic fibers.

The novel compositions, shaped articles and assemblies can be used to expose or release a second component which is distributed in or encapsulated by the TPE, especially in response to an increase in temperature from below T_(q) to above T_(q). Second components which can thus be exposed or released include herbicides, seeds, perfumes, deodorizers, pest control agents, fungicides, insecticides, fertilizers and other agrichemicals, disinfectants, and pharmaceuticals. Thus specific applications include coating formulations to control water transmission to seeds, animal ear tags, collars and harnesses to release pest control agents, and microcapsules to release agrichemicals in response to temperature changes.

Another important use for certain of the novel TPE's is to occlude a channel in a mammal, and like uses, as disclosed in the Schmitt application No. 939,100 incorporated herein by reference.

Other applications include the production of pharmaceutical and medical products in a form which is satisfactory for ingestion, implantation, skin attachment or the like, which can be readily processed at selected temperatures well below the degradation temperature of the product , and which is sufficiently elastomeric to prevent brittle fracture and flaking.

Other specific applications include flexible commercial products like shoe soles, clothing, weather stripping, gasketing, sealants, caulking, expansion joints, roofing membranes, cable insulation, and the like. The novel TPE's can have T_(q) 's which are above the maximum temperatures to which such products are exposed in use, but which allow the TPE to be processed at lower temperatures than the TPE's currently used for such applications. They can therefore be processed more economically. For example TPE shoe soles are currently processed at 100° C. and through use of the new TPE's could be processed at 70° C.

For a detailed description, including Examples, of the ninth, tenth and eleventh aspects of the invention, reference should be made to Application Ser. Nos. 07/654,723, 07/829,494 and 07/928,800 by Schmitt et al, Application Ser. No. 07/885,915 by Stewart, and Application Ser. No. 07/939,110 by Schmitt, respectively.

The invention is illustrated in the following Examples.

EXAMPLES

In Examples 1-6, the ingredients and amounts thereof (in grams) shown in Table 1 were reacted to form a TPE of the invention having the properties shown in Table 1. In Table 1, POLY-THF 650, POLY-THF 2000 and POLY-THF 4500 are polyethers of different molecular weights which are obtained by polymerizing tetrahydrofuran and which are commercially available from BASF. In Examples 1-4, the hard blocks were formed by polymerization of an acrylate monomer on a polyurethane elastomer obtained by reaction of POLY-THF with a diisocyanate. In Examples 5 and 6, a preformed hard block polymer was functionalized by reaction with a diisocyanate and then reacted with POLY-THF.

In Examples 7 to 31 and 33-46, the first step was to make a hard block SCC acrylate and/or methacrylate polymer, using the ingredients and amounts thereof (in grams) shown in Table 2 to make one of the SCC polymers H1 to H19 having the properties shown in Table 2. The SCC polymer was then functionalized by reaction with isocyanatoethylmethacrylate (IEMA).

In Examples 7 to 31, the TPE was then prepared by copolymerizing butyl acrylate and the functionalized hard block polymer, using the amounts shown in Table 3, to give a TPE having the properties shown in Table 3. In Examples 33--49, the TPE was prepared by copolymerizing the ingredients and amounts thereof shown in Table 4, to give a TPE having the properties shown in Table 4.

Further details of the procedures in the Examples are given below.

Example 1

The POLY-THF 650, toluene (500 mL) and dibutyl tin dilaurate (1 drop) were added to a 1-litre flask equipped with a stirrer, a Dean-Stark water separator and a drying tube. The toluene was distilled from the flask into the separator to remove water. After cooling, the diisocyanate was injected into the reaction mixture, which was then stirred at room temperature for 22 hours; the reaction was monitored by infra-red (IR) spectroscopy, observing the isocyanate peak at 2270 cm⁻¹. The amine was then added as a solution in about 10 mL of warm toluene. After the reaction mixture had been at room temperature for 24 hours, the acrylate monomer and AIBN (present as an initiator) were added, and nitrogen was bubbled through the mixture for 8 minutes. The reaction mixture was heated to 60° C. for 18 hours, with stirring. After cooling, the mixture was poured into 1 litre of heptane, and the TPE was recovered as a precipitate.

Example 2

The POLY-THF 650 and toluene (70 mL) were added to a 100 mL flask fitted with a stirrer and a Dean-Stark water separator, and 25 mL of toluene were distilled from the flask into the water separator under nitrogen to remove water. The mixture was cooled and the separator was replaced with a serum cap and a drying tube. The diisocyanate and one drop of dibutyl tin dilaurate were added, and the reaction mixture was stirred at room temperature for 21 hours. To the resulting solution was added the amine (as a solution in 5 mL of warm toluene). The solution was stirred at room temperature for 2.5 hours, at which time no isocyanate could be detected by IR spectroscopy. The solution was transferred to a screw-capped bottle fitted with a stirrer, and the acrylate and AIBN were added. The bottle was sealed and then heated to 60° C. for 18 hours with stirring. After cooling, the mixture was poured into heptane, and the TPE was recovered as a precipitate which was dried under vacuum at room temperature.

Example 3

The procedure of Example 2 was followed, with the following modifications: (1) 35 mL of toluene were added instead of 70 mL; (2) after addition of the diisocyanate, the mixture was stirred for 23.5 hours, instead of 21 hours; (3) toluene (30 mL) was added to the viscous solution which was then heated to 60° C. before adding the amine; (4) the amine-containing solution was stirred for 48 hours, instead of 2.5 hours, at room temperature; and (5) the mixture was poured into ethyl alcohol, instead of heptane, to recover the TPE.

Example 4

The procedure of Example 2 was followed, with the following modifications: (1) 55 mL of toluene were added, instead of 70 mL;.(2) after addition of the diisocyanate, the mixture was stirred for 4 hours at 40° C., instead of 21 hours at room temperature; and (3) after addition of the amine to the viscous solution at 40° C., the mixture was heated for 2 hours at 40° C. instead of 2.5 hours at room temperature.

Example 5

The poly (1,2-octadecene epoxide), M_(n) 2579, and toluene (100 mL) were placed in 500 mL flask fitted with a stirrer, a Dean-Stark water separator and a nitrogen inlet. 25 mL of the toluene were distilled into the separator to remove water. The separator was then replaced by a stopper. The diisocyanate, dissolved in 8 mL of toluene, and one drop of dibutyl tin dilaurate were added. The mixture was heated to 75° C. with stirring for 2 hours 40 minutes, after which time no change could be detected by IR spectroscopy. A solution of the POLY-THF in 100 mL toluene was dried by distilling 25 mL of the toluene into a water separator, and the dried solution was added to the 75° C. solution of the isocyanate-modified hard block polymer. The reaction mixture was maintained at 75° C. for 0.5 hour, and after cooling was poured into heptane. The TPE was recovered as a precipitate which was dried under vacuum at room temperature.

Example 6

The procedure of Example 5 was followed with the following modifications: (1) the poly(1,2-octadecene epoxide), M_(n) 2261 instead of 2579, was placed in the flask with 105 mL, instead of 100 mL, of toluene; (2) the diisocyanate was dissolved in 10 mL, instead of 8 mL, of toluene; (3) the mixture was heated to 70° C. for 1 hour, instead of 75° C. for 2 hours 40 minutes; (4) 85 mL, instead of 100 mL, of toluene was used in preparing the solution of POLY-THF; (5) the reaction mixture was maintained at 70° C. for 2 hours, instead of 75° C. for 0.5 hour; and (6) the cooled reaction mixture was poured into ethanol, instead of heptane, to recover the TPE.

Examples 7-46

Preparation of Hard Block SCC Polymers H1 to H19

SCC polymer Hi was prepared by adding the docosanyl acrylate (100 g), mercaptoethanol (3.6 g) as capping agent, and AIBN (1 g) as initiator, to toluene (200 mL), and heating the reaction mixture with reflux under nitrogen at 60° C. for 16 hours with stirring. The SCC polymer was isolated and heated with IEMA (8 g) in toluene for 16 hours at 70° C., to give a functionalized hard block polymer.

SCC polymers H2 to H19 were made similarly, with appropriate modifications, e.g. to control the molecular weight. For example, SCC polymer H2 was prepared by the above procedure with the following modifications: (1) after the reaction mixture had been heated at 60° C. for 16 hours, it was heated at 80° C. for 16 hours to degrade residual AIBN; (2) 3 drops of dibutyl tin dilaurate were added with the IEMA; and (3) the reaction with the IEMA was conducted at 25° C. for 16 hours, instead of 70° C. for 16 hours. SCC polymer H16 was prepared by the above procedure with the following modifications: (1) the amount of toluene was 1000 mL and the amount of mercaptoethanol was 5.2 g; (2) the heating at 60° C. for 16 hours was followed by heating at 80° C. for 6 hours; and (3) the SCC polymer was functionalized by heating with IEMA (34 g) and dibutyl tin dilaurate (0.2 g) at 30° C. for 16 hours. The SCC polymer H17 was prepared by the above procedure with the following modifications: (1) the amount of toluene was 300 mL, the amount of mercaptoethanol was 1.5 g and the amount of AIBN was 0.3 g; (2) the heating at 60° C. for 16 hours was followed by heating at 80° C. for 8 hours; and (3) the SCC polymer was functionalized by heating with IEMA (10 g) and dibutyl tin dilaurate (7 drops) at 60° C. for 16 hours. The SCC polymer H18 was made by adding C16A (120 g), C18A (30 g), mercaptoethanol (1.5 g) and AIBN (1.5 g) to toluene (300 mL); heating at 60° C. for 16 hours and then at 80° C. for 6 hours; cooling; adding IEMA (12.75 g); and stirring at room temperature for 16 hours. The SCC polymer H19 was made by adding C22A (100 g), mercaptoethanol (1 g) and AIBN (1 g) to toluene (200 mL); heating at 60° C. for 16 hours, and then at 80° C. for 6 hours; cooling; adding IEMA (8.5 g) and dibutyltin dilaurate (5 drops); and stirring at room temperature for 16 hours.

Preparation of the TPE's

The TPE of Example 7 was prepared by adding the functionalized SCC polymer H1 (40 g), the butyl acrylate (60 g) and AIBN (1 g) to toluene (200 mL), and heating at 60° C. for 16 hours with stirring. The reaction mixture was cooled and poured into ethanol to recover the TPE as a precipitate, and the precipitate was dried at elevated temperature under reduced pressure. The TPE's of Examples 8-31 were prepared similarly, with appropriate modifications (e.g. the addition of dodecyl mercaptan as a chain transfer agent to control molecular weight).

In Examples 33-40, the H16 functionalized SCC polymer, EHA and HEA, in the amounts shown in Table 4, were added to a reaction vessel, together with ethyl acetate (100 g), heptane (100 g) and AIBN (0.15 g), and heated at 60° C. for 16 hours under nitrogen. The polymer was recovered as in Example 7.

In Example 41, the indicated amounts of H16, EHA, HEA and MPEG were added to a reaction vessel, together with ethyl acetate (140 g), heptane (60 g) and AIBN (0.2 g), and heated at 60° C. for 16 hours.

In Example 42, the indicated amounts of H18, EHA, HEA and MBA were added to a reaction vessel, together with ethyl acetate (112 g), heptane (48 g) and AIBN (0.1 g), and heated at 55° C. for 16 hours and then at 75° C. for 1 hour.

In Example 43, H17 (63.4 g), C12A (119 g), C14A (127 g) and AA (7.6 g) were added to a reaction vessel, together with ethyl acetate (475 g) and AIBN (0.3 g), and heated at 60° C. for 7 hours and then at 75° C. for 7 hours. The polymer, which contained 20% of H17, had a crystalline soft block with a T_(ms) of about 6° C. (and onset of melting at 2° C.) resulting from the C12A and C14A units and a crystalline hard block with a T_(q) of about 61° C. (and onset of melting at about 54° C.) resulting from the H17 (C22A) macromer.

In Example 44, the indicated amounts of H16, EHA and HEA were added to a reaction vessel, together with ethylacetate (140 g), heptane (60 g), and AIBN (0.15 g), and heated at 60° C. for 16 hours.

In Example 45, the indicated amounts of H19, EHA and HEA were added to a reaction vessel, together with ethyl acetate (60 mL), heptane (140 mL) and AIBN (0.5 g), and heated at 60° C. for 16 hours.

In Example 46, the indicated amounts of H19, EHA and AA were added to a reaction vessel, together with toluene (180 g) and AIBN (0.5 g), and heated at 60° C. for 16 hours.

Copolymers C1-C13 are random high molecular weight acrylate polymers. Typically they were prepared by adding the monomers and amounts thereof in Table 5 to a reaction vessel, together with ethyl acetate (100 g), heptane (100 g) and AIBN (0.15 g) and heating the reaction mixture at 60° C. for 16 hours under nitrogen. The copolymer was recovered by pouring the cooled reaction mixture into ethanol and drying the precipitate at elevated temperature under reduced pressure.

Preparation of Copolymers WOC1, WOC2 and WOC3

Copolymers WOC1, WOC2 and WOC are low molecular weight random SCC polymers which can be added to PSA's to reduce peel strength on warming. They were prepared in the same general way as C1-C13, using the monomers and amounts thereof shown in Table 6, but taking steps to control the molecular weight.

Preparation and Testing of PSA's

A number of PSA composites were made and tested, as summarized in Table 7 below. Table 7 shows the results for PSA composites in which the PSA comprises a TPE containing SCC hard blocks. A number of the PSA's also contained one of the crystalline SCC additives ("cryst. SCC") WOC1, WOC2 or WOC3. Table 8, which is included for comparison, shows results for comparable PSA's which do not include such SCC hard blocks. Table 9 shows the results of testing on human skin.

Except for PSA composite No. QA141, the PSA composites were made and tested as follows. The specified polymer(s) was dissolved in a suitable solvent, e.g. toluene or heptane, to give a homogeneous, bubble-free composition with a solids content of about 45%. The composition was applied to a polyester TPE ("Hytrel 4056") film 1.75 mil (0.0045 cm) thick, in the following way. The film was secured to a flat glass plate 18×12 inch (46×30.5 cm) and smoothed to remove air bubbles between the film and the plate. A wire-wound applicator rod (No. 70 Gardco Wet Film Applicator Rod) was then used to apply a coating of the composition to the film. The coating was dried in an oven at 90° C. for 30 minutes or more. The dried coating thickness was about 1.6 to 1.8 mil (0.0040 to 0.0046 cm). The coating was covered with a siliconized polyethylene-impregnated paper. The resulting laminate was removed from the glass plate and samples about 4.0×0.5 inch (10×1.25 cm) were cut from the laminate.

PSA composite QA141 was made by coating PSA QA112 by the method described above to give a coating 1 mil thick. This coating was then covered by a coating about 3 microns thick of PSA QA11, by transfer coating from a siliconized Mylar film.

The PSA composites were tested as previously described.

Preparation and Heat Sealing of Films of TPE's

The TPE of Example 43 was formed into a film as follows. The polymer (10 g) was dissolved in a mixture of toluene (12.5 mL) and heptane (12.5 mL), coated onto a siliconized polyester backing and dried at 90° C. The dried film was transferred to a microporous support (Cellgard K878). The random copolymer C13 was formed into a film in the same way. The Example 43 film could readily be heat-sealed to a commercially available film of a blend of polyethylene (PE) and ethylene/vinyl acetate copolymer (EVA). The copolymer C13 film gave a markedly inferior heat seal. The oxygen permeabilities of the Example 43 film and the PE/EVA film were measured and are shown below (in cc.ml/100 in² ·atm·24 hrs).

    ______________________________________                                                      at 45° F.                                                                      at 72° F.                                           ______________________________________                                         Example 43     1800     5150                                                   PE/EVA         270      650                                                    ______________________________________                                    

                  TABLE 1                                                          ______________________________________                                                      EXAMPLE NO.                                                                    1    2      3      4    5    6                                    ______________________________________                                         SOFT BLOCK                                                                     INGREDIENTS                                                                    (i) Starting Polyether                                                         POLY-THF 650   100    10.0   --   10.0 --   25.22                              POLY-THF 4500  --     --     10.0 --   --   --                                 POLY-THF 2000  --     --     --   --   41.68                                                                               --                                 (ii) tolylene-2,4-                                                                            27.82  2.78   0.47 2.77 --   --                                 diisocyanate                                                                   (iii) amine                                                                    2-aminoethane thiol                                                                           0.783  --     --   --   --   --                                 cysteamine     --     0.175  0.064                                                                               0.083                                                                               --   --                                 HARD BLOCK                                                                     INGREDIENTS                                                                    C18A           42.71  3.89   3.84 --   --   --                                 C22A           --     --     --   3.99 --   --                                 AIBN           0.433  0.04   0.04 0.01 --   --                                 poly-1,2-      --     --     --   --   11.71                                                                               8.7                                octadecene epoxide                                                             methylene-diphenylene                                                                         --     --     --   --   5.78 10.19                              diisocyanate                                                                   PROPERTIES OF                                                                  TPE PRODUCT                                                                    M.sub.w        65k    153k   181k 66k  74   47                                 M.sub.w /M.sub.n                                                                              1.8    1.7    3.4  1.8  1.5  1.7                                DSC onset °C. (T.sub.o)                                                                --     --     --   --   45   34.3                               DSC peak °C. (T.sub.q)                                                                 48.2   45     48*  61   47.9†                                                                        39.4                               DSC heat of fusion J/g                                                                        3.7    1.7    14   4.9  8.6  20.9                               ______________________________________                                          *The TPE of Example 3 also showed a peak at 24.3° C. which was          attributable to the crystallinity of the POLYTHF in the soft block.            †The TPE of Example 5 also showed a peak at 21.7° C. which       was attributable to the crystallinity of the POLYTHF in the soft block.  

                                      TABLE 2                                      __________________________________________________________________________              HARD BLOCK TYPE                                                                H1 H2 H3  H4 H5 H6  H7 H8  H9 H10                                     __________________________________________________________________________     HARD BLOCK                                                                     INGREDIENTS                                                                    C16A     -- 8  --  -- -- --  -- --  -- --                                      C18A     -- 92 100 -- 15 25  -- --  -- --                                      C22A     100                                                                               -- --  -- -- --  -- 100 -- --                                      C18MA    -- -- --  100                                                                               85 75  66 --  -- --                                      C22MA    -- -- --  -- -- --  -- --  -- --                                      C22 IEMA -- -- --  -- -- --  34 --  100                                                                               --                                      C30 IEMA -- -- --  -- -- --  -- --  -- 100                                     C4A      -- -- --  -- -- --  -- --  -- --                                      HARD BLOCK                                                                     PROPERTIES                                                                     M.sub.w  4300                                                                              3900                                                                              3900                                                                               3900                                                                              3600                                                                              3900                                                                               4300                                                                              9700                                                                               6000                                                                              3100                                    M.sub.w /M.sub.n                                                                        1.26                                                                              1.34                                                                              1.33                                                                               1.32                                                                              1.32                                                                              1.33                                                                               1.3                                                                               1.37                                                                               1.3                                                                               1.4                                     DSC onset °C.                                                                    57 39 42  33 33 33  34 65  71 72                                      DSC peak °C. (T.sub.m)                                                           62 42 45  36 36 37  42 67  74 79                                      Heat of fusion J/g                                                                      133                                                                               83 118 74 76 79  69 108 103                                                                               159                                     __________________________________________________________________________              HARD BLOCK TYPE                                                                H11                                                                               H12                                                                               H13 H14                                                                               H15                                                                               H16 H17                                                                               H18 H19                                        __________________________________________________________________________     HARD BLOCK                                                                     INGREDIENTS                                                                    C16A     -- -- 80  -- -- 400 -- 120 --                                         C18A     -- -- 20  -- 80 100 -- 30  --                                         C22A     -- -- --  -- -- --  150                                                                               --  100                                        C18MA    76 50 --  80 -- --  -- --  --                                         C22MA    -- 50 --  20 -- --  -- --  --                                         C22 IEMA 24 -- --  -- --     -- --  --                                         C30 IEMA -- -- --  -- -- --  -- --  --                                         C4A      -- -- --  -- 20     -- --  --                                         HARD BLOCK                                                                     PROPERTIES                                                                     M.sub.w  5900                                                                              5300                                                                              12,300                                                                             5500                                                                              8900                                                                              13,100                                                                             6700                                                                              11,700                                                                             9000                                       M.sub.w /M.sub.n                                                                        1.29                                                                              1.35                                                                              1.65                                                                               1.29                                                                              1.6                                                                               1.66                                                                               1.2                                                                               1.56                                                                               1.27                                       DSC onset °C.                                                                    35 43 35  31 32 35                                                    DSC peak °C. (T.sub.m)                                                           42 47 38  36 38 38  63                                                Heat of fusion J/g                                                                      57 72 67  58 45                                                       __________________________________________________________________________

                                      TABLE 3                                      __________________________________________________________________________                 PROPERTIES OF TPE                                                  INGREDIENTS OF TPE                                                                               DSC                                                          Hard     Soft     T.sub.o                                                                            T.sub.q                                                                            Heat of                                                                            XL TS   YM                                       Ex.                                                                               Block Block M.sub.w                                                                           (Onset)                                                                            (Peak)                                                                             Fusion                                                                             Time                                                                              kg/                                                                               El                                                                               kg/                                      No.                                                                               Type                                                                              Amt                                                                               Amt                                                                               M.sub.w                                                                           M.sub.n                                                                           °C.                                                                         °C.                                                                         J/g sec                                                                               cm.sup.2                                                                          % cm.sup.2                                 __________________________________________________________________________      7 H1 40 60 179k                                                                              4.83                                                                              57  62  45  -- 22 53                                                                               105                                       8 H11                                                                               40 60 96k                                                                               3.5                                                                               34  39  16  -- -- --                                                                               --                                        9 H3 40 60 184k                                                                              5.9                                                                               38  43  28  >15                                              10 H3 40 60 48k                                                                               2.3                                                                               39  42  33  >15                                              11 H3 40 60 103k                                                                              3.9                                                                               37  43  30  >15                                              12 H4 40 60 40k                                                                               2.2                                                                               37  41  28  16                                               13 H4 40 60 80k                                                                               3.1                                                                               38  41  28  24                                               14 H5 40 60 48k                                                                               3.0                                                                               30  33  16  54                                               15 H6 40 60 52k                                                                               2.5                                                                               30  33  17  29                                               16 H6 30 70 56k                                                                               2.6                                                                               29  32  11  51                                               17 H4 30 70 55k                                                                               2.6                                                                               27  29  9   97                                               18 H6 20 80 57k                                                                               2.8                                                                               28  31  9   135                                              19 H4 20 80 53k                                                                               2.3                                                                               25  29  8   154                                              20 H7 40 60 55k                                                                               2.1                                                                               38  43  13  25                                               21 H7 30 70 64k                                                                               2.1                                                                               36  42  13  25                                               22 H7 20 80 63k                                                                               2.0                                                                               35  40  6   17                                               23 H7 30 70 96k                                                                               2.8                                                                               37  43  10  20                                               24 H1 50 50 173k                                                                              4.96                                                                              58  63  50  -- 28 33                                                                               187                                      25 H1 30 70 176k                                                                              4.49                                                                              58  62  39  -- 18 86                                                                               74                                       26 H8 40 60 168k                                                                              4.54                                                                              62  66  48  -- 14 94                                                                               67                                       27 H8 40 60 51k                                                                               1.88                                                                              63  65  57  -- 11 14                                                                               159                                      28 H8 40 60 97k                                                                               3.14                                                                              63  65  56  -- 15 35                                                                               162                                      29 H8 40 60 168k                                                                              4.57                                                                              62  66  48  -- 14 94                                                                               66                                       30 H9 50 50 310k                                                                              13.4                                                                              64  69  44  -- 68 37                                                                               607                                      31 H10                                                                               30 70 178k                                                                              9.7                                                                               65  79  36  -- 33 42                                                                               261                                      __________________________________________________________________________

Examples 32A, B and C

A. A composition containing RDX (an explosive), 75 parts, and a TPE of the invention having a T_(q) of 74° C., 25 parts, can be made as follows. The TPE is heated to about 84° C. in a high shear mixer; half the RDX is added and mixed with the TPE for 20 minutes; the remainder of the RDX is then added and mixing is continued until a uniform composition is obtained. The mixture does not have a restricted pot life at 84° C. It can be shaped by extrusion to give a solid with an elongation of 20% or more. The formed product, and scrap, can be reprocessed.

B. Seed-containing compositions can be prepared by dissolving a TPE of the invention in a suitable solvent (e.g. 2 g of TPE in 5 mL of a 1/1 mixture of heptane and ethyl acetate), using the solution to coat the seeds (e.g. by placing bush beans in a vessel and adding the solution), and drying the seeds, which are thus provided with a thin continuous coating of the TPE.

C. The complex modulus of a TPE of the invention having a T_(q) of 48° C. was measured at various temperatures at 0.05 radians/second, with the following results:

    ______________________________________                                         Temperature 40        53         67   80                                       Complex     50,000,000                                                                               2000       1000 2000                                     Modulus                                                                        ______________________________________                                    

The complex modulus of an SCC hard block polymer having a T_(m) of 43° C. was measured at various temperatures at 0.01 radians/second, with the following results:

    ______________________________________                                         Temperature 40        50         75  100                                       Complex     50,000,000                                                                               100        20  5                                         Modulus                                                                        ______________________________________                                    

                  TABLE 4                                                          ______________________________________                                              Hard                                                                      Ex   Block         Soft Block       M.sub.w                                    No.  Type   Amt    EHA  AA   HEA  Mw    M.sub.n                                                                              Viscosity                        ______________________________________                                         33   H16    1      94   5    --   488k  6.6   231                              34   H16    2      93   5    --   700k  11.0  587                              35   H16    3      92   --   5    557k  4.4   --                               36   H16    3      92   5    --   1100k 2.5   1313                             37   H16    5      90   5    --   967k  4.0   2600                             38   H16    5      87   --   8.2  895k  2.86  --                               39   H16    5      87   --   8    554k  19.4  --                               40   H16    5      87   --   8    >1000k                                                                               14.1  25.6k                            41   H16    5      82   --   8+   --    --    >10k                             42   H18    5      62   --   8+   721k  9.4   5350                             43   H17    20     80++ --   --   326k  --    --                               44   H16    5      87   --   8    895k  2.85  1960                             45   H19    5      87   --   8    --    --    --                               46   H19    6      108  6    --   272k  3.8   --                               ______________________________________                                          +In Examples 41 and 42, the soft block monomers also included 5 g MPEG         (Example 41) or 25 g MBA (Example 42)                                          ++In Example 43, the soft block was formed from C12A, C14A and AA              (50/47/3)                                                                

                  TABLE 5                                                          ______________________________________                                         Ingredients                                                                                            C4A/C14                                                Copolymer                                                                              EHA     HEA     A/C18A AA    M.sub.w                                                                              M.sub.w /M.sub.n                    ______________________________________                                         C1      92      8       --     --    1200k 2.38                                C2      96      4       --     --    318k  7.7                                 C3      92      8       --     --    401k  3.2                                 C4      95      --      --     5     1002k 1.76                                C5      92      8       --     --    504k  4.3                                 C6      92      8       --     --    1750k 1.7                                 C7      92      8       --     --    >1000k                                                                               --                                  C8      92      8       --     --    882k  4.9                                 C9      87      5       8 (C18A)                                                                              --    984k  5.9                                 C10     90      --      5 (C18A)                                                                              5     --    --                                  C11     47      --      47 (C4A)                                                                              6     >1000k                                                                               --                                  C12     97      --      --     3     629k  6.21                                C13     47      --      3 (C14A)                                                                              --                                              ______________________________________                                    

C9 had a viscosity of 3000 cps. C10 had a viscosity of 400 cps.

                  TABLE 6                                                          ______________________________________                                                 Ingredients                                                            Copolymer C16A     C18A   AA     M.sub.w                                                                             M.sub.w /M.sub.n                         ______________________________________                                         WOC1      54.1     40.9   5.0    2.5 k                                                                               1.48                                     WOC2      54.1     40.9   5.0    3.7 k                                                                               1.5                                      WOC3      95       --     5      2 k  1.57                                     ______________________________________                                    

                  TABLE 7                                                          ______________________________________                                                    POLYMERS                                                                         Base          Cryst.     PROPER-                                         PSA   Resin         SCC        TIES                                            No.   Type   Amt    Type  Amt  Shear Tack                               ______________________________________                                         A1. Base Resin                                                                 is EHA/AA/                                                                     H16, (95-x)/5/x                                                                x = 1    QA11    Ex 33  100  --    --   180   16                               x = 2    QA12    Ex 34  100  --    --   916   14                               x = 3    QA13    Ex 36  100  --    --   1637  11                               x = 5    QA14    Ex 37  100  --    --   >10k  >30                              A2. Base Resin                                                                          QA21    Ex 33  100  --    --   180   16                               is EHA/AA/                                                                              QA22    Ex 33  90   WOC1  10   329                                    H16, 94/5/1                                                                             QA23    Ex 33  80   WOC1  20   694                                             QA24    Ex 33  70   WOC1  30   611                                    A3. Base Resin                                                                          QA31    Ex 34  100  --    0    916   14                               is EHA/AA/                                                                              QA32    Ex 34  90   WOC1  10   2060                                   H16, 93/5/2                                                                             QA33    Ex 34  80   WOC1  20   2719                                            QA34    Ex 34  70   WOC1  30   2774                                   A4. Base Resin                                                                          QA41    Ex 35  100  --    0    470   12                               is EHA/HEA/                                                                             QA42    Ex 35  90   WOC1  10   1143                                   H16, 92/5/3                                                                             QA43    Ex 35  80   WOC1  20   1575                                            QA44    Ex 35  70   WOC1  30   2770                                   A5. Base Resin                                                                          QA51    Ex 37  100  --    0    >10k  >30                              is EHA/AA/                                                                              QA52    Ex 37  90   WOC1  10   20,000                                 H16, 90/5/5                                                                             QA53    Ex 37  80   WOC1  20   --                                              QA54    Ex 37  70   WOC1  30   27,000                                 A6. Base Resin                                                                          QA61    Ex 39  100  --    0    595   1.6                              is EHA/HEA/                                                                             QA62    Ex 39  90   WOC1  10   787                                    H16, 87/8/5                                                                             QA63    Ex 39  80   WOC1  20   957                                             QA64    Ex 39  70   WOC1  30   672                                             QA65    Ex 40  100  WOC1  0    2090                                            QA66    Ex 40  75   WOC1  25   >86k                                            QA67    Ex 40  75   WOC1  25   139k                                   A7. Base Resin                                                                          QA71    Ex 41  100  --    --   1900  9.76                             is EHA/HEA/                                                                             QA72    Ex 41  75   WOC2  25   2820  --                               H16, MPEG,                                                                     82/5/8/5                                                                       A8. Base Resin                                                                          QA81    Ex 42  100  --    --   5055  16.3                             is EHA/HEA/                                                                             QA82    Ex 42  75   WOC2  25   >86k                                   H16, 3MBA,                                                                     62/8/5/25                                                                      A9. Base Resin                                                                          QA91    Ex 46  100  --    --   1722  3.4                              is EHA/HEA/                                                                             QA92    Ex 46  75   WOC2  25   >86k  --                               H19, 87/8/5                                                                             QA93    Ex 46  37.5                                                                    C6     12.5                                                                    C7     12.5                                                                    C8     12.5 WOC2  25   717                                    A10. Base Re-                                                                           QA101   Ex 46  100  --    --   1655  10                               sin is EHA/                                                                             QA102   Ex 46  80   WOC1  20   3844  --                               AA/H19,                                                                        90/5/5                                                                         ______________________________________                                    

                  TABLE 8                                                          ______________________________________                                                     POLYMERS                                                                         Base          Cryst.     PROPER-                                         PSA   Resin         SCC        TIES                                              No.     Type   Amt  Type  Amt  Shear                                                                               Tack                             ______________________________________                                         B1. Base Resin is                                                                        QB11    C2     100  --    0    --   --                               EHA/HEA 96/4                                                                   B2. Base Resin is                                                                        QB21    C3     100  --    0    --   1.9                              EHA/HEA 92/8                                                                   B3. Base Resin is                                                                        QB31    C4     100  --    0    701  2.8                              EHA/HEA 95/5                                                                             QB32    C4     80   WOC1  20   524                                             QB33    C4     70   WOC1  30   495                                             QB34    C4     60   WOC1  40   399                                   B4. Base Resin is                                                                        QB41    C5     100  --    0    0                                     EHA/HEA 92/8                                                                             QB42    C5     90   WOC1  10   0                                               QB43    C5     80   WOC1  20   0                                               QB44    C5     70   WOC1  30   0                                     B5. Base Resin is                                                                        QB51    C9     100  --    0    12.6 1.1                              EHA/HEA/C18A,                                                                            QB52    C9     75   WOC2  25   23   --                               87/8/5                                                                         B6. Base Resin is                                                                        QB61    C10    100  --    0    148  14.1                             EHA/HEA/C18A,                                                                            QB62    C10    75   WOC2  25   164                                   90/5/5                                                                         B7. Base Resin is                                                                        QB71    C1     75   WOC3  25   17                                    EHA/HEA, 92/8                                                                  B8. Base Resin is                                                                        QB81    C4     63                                                    EHA/AA, 95/5+     C12    7    WOC3  30   312                                   EHA/AA 97/3                                                                    B9. Base Resin is                                                                        QB91    C6     25                                                    EHA/HEA, 92/8     C7     25                                                                      C8     25   WOC2  25   77                                    ______________________________________                                                     POLYMERS                                                                         Base                     PROPER-                                         PSA   Resin         TPE        TIES                                              No.     Type   Amt  Type  Amt  Shear                                                                               Tack                             ______________________________________                                         B10. Base Resin                                                                          QB101   C2     99   WOC2  1         4.5                              is EHA/HEA,                                                                              QB102   C2     97   WOC2  3         6.0                              96/4      QB103   C2     95   WOC2  5         11.0                                       QB104   C2     90   WOC2  10        25.3                                       QB105   C2     75   WOC2  25        >30                              B11. Base Resin                                                                          QB111   C3     99   WOC2  1         2.8                              is EHA/HEA,                                                                              QB112   C3     97   WOC2  3         12.9                             92/8      QB113   C3     95   WOC2  5         18.7                                       QB114   C3     90   WOC2  10        20.4                                       QB115   C3     75   WOC2  25        30.0                             B12. Base Resin                                                                          QB121   C11    100  --    --   600  10                               is EHA/C4A/                                                                    AA, 47/47/6                                                                    ______________________________________                                    

                                      TABLE 9                                      __________________________________________________________________________     Peel Strengths of PSA's on Human Skin                                                   PSA Adhesive                                                                   QA67                                                                               QB71                                                                               QB81                                                                               QA92                                                                               QA93                                                                               QB91                                                                               QA101                                                                              QB121                                                                              QA141                                 __________________________________________________________________________     After 0.5 hr, at LT                                                                     --  60  --  --  --  --  --  --  --                                    at HT    --  6   --  --  --  --  --  --  --                                    % reduction                                                                             --  90% --  --  --  --  --  --  --                                    After 1 hr, at LT                                                                       29  --  23.8                                                                               14  40  55  43  44  26                                    at HT    3   --  3.4 2   5.5 2.5 --  --  2.1                                   % reduction                                                                             89% --  86% 85% 26% 95% --  --  92%                                   After 24 hr, at LT                                                                      80  211 89  --  95  --  79.5                                                                               78  --                                    at HT    9.5 21  29  --  9   --  --  --  --                                    % reduction                                                                             88% 90% 67% --  91% --  --  --  --                                    After 48 hr, at LT                                                                      90  --  89  --  --  --  --  --  --                                    at HT    12  --  38  --  --  --  --  --  --                                    % reduction                                                                             87% --  57  --  --  --  --  --  --                                    Sheer Strength                                                                          139k                                                                               17  312 >86k                                                                               717 77  1655                                                                               600 1906                                  __________________________________________________________________________ 

We claim:
 1. A pressure-sensitive adhesive (PSA) composite which comprises(i) a flexible backing, (ii) a solvent-free layer of a PSA which is secured to the backing, and which comprises a thermoplastic elastomer (TPE) or is at least partially covered by a layer comprising a TPE, said TPE comprising polymeric molecules which comprise(i) polymeric A blocks which(a) are crystalline and have a melting point T_(q), or (b) are amorphous and have a glass transition point T_(gh) ; (ii) at least one polymeric B block which is linked to at least two A blocks and which(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C. or (b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C.;wherein at least one block selected from the A and B blocks comprises a side chain comprising crystallizable moieties which render the block crystalline.
 2. A PSA composite according to claim 1 wherein the PSA contains, in addition to the TPE, a crystalline polymer additive which has a weight average molecular weight of less than 25,000, a melting point of 23° C. to 120° C., and a heat of fusion of at least 5 Joules/g.
 3. A PSA composite according to claim 2 wherein the crystalline polymer additive is a side chain crystallizable polymer having a melting point of 30 to 60° C. and a heat of fusion of at least 20 Joules/g.
 4. A PSA composite according to claim 2 wherein the PSA contains 1 to 50% by weight of the crystalline polymer additive.
 5. A PSA composite according to claim 1 wherein the PSA contains, in addition to the TPE, an amorphous polymer.
 6. A PSA composite according to claim 5 wherein the amorphous polymer is an acrylic adhesive.
 7. A PSA composite according to claim 5 wherein the amorphous polymer is selected from olefin copolymers; polysiloxanes; polyurethanes; polymers of vinyl esters; polyamides; natural rubbers; synthetic rubbers; styrene/butadiene latex-based adhesives, thermoplastic rubbers of the ABA block copolymer type, where A represents a thermoplastic styrene end block and B represents a rubber midblock of polyisoprene, polybutadiene or poly(ethylene/butylene); butyl rubber; polyisobutylene; and polymers and copolymers of vinyl ethers.
 8. A PSA composite according to claim 1 wherein the PSA contains, in addition to the TPE,(a) 1 to 50% by weight of a crystalline polymer additive which has a weight average molecular weight of less than 25,000, a melting point of 23° C. to 120° C., and a heat of fusion of at least 5 Joules/g; and (b) an amorphous polymer which is an acrylic adhesive.
 9. A PSA composite according to claim 1 wherein the PSA contains, in addition to the TPE,(a) 1 to 50% by weight of a crystalline polymer additive which has a weight average molecular weight of less than 25,000, a melting point of 23° C. to 120° C., and a heat of fusion of at least 5 Joules/g; and (b) an amorphous polymer which is selected from olefin copolymers; polysiloxanes; polyurethanes; polymers of vinyl esters; polyamides; natural rubbers; synthetic rubbers; styrene/butadiene latex-based adhesives, thermoplastic rubbers of the ABA block copolymer type, where A represents a thermoplastic styrene end block and B represents a rubber midblock of polyisoprene, polybutadiene or poly(ethylene/butylene); butyl rubber; polyisobutylene; and polymers and copolymers of vinyl ethers.
 10. A PSA composite according to claim 1 wherein the B block in the TPE comprises 50 to 100% by weight of units derived from at least one n-alkyl acrylate, n-alkyl acrylamide, n-alkyl methacrylate, or n-alkyl methacrylamide in which the n-alkyl group contains 4 to 16 carbon atoms, and the A block comprises 50 to 100% by weight of units derived from at least one n-alkyl acrylate, n-alkyl acrylamide, n-alkyl methacrylate, or n-alkyl methacrylamide, in which the n-alkyl group contains at least 16 carbon atoms.
 11. A PSA composite according to claim 10 wherein the B blocks comprise 75 to 100% by weight of units derived from C12 Acrylate or C14 Acrylate or both, and the A blocks comprise 75 to 100% of units derivable from C22 Acrylate.
 12. A PSA composite according to claim 1 wherein each of the A blocks is amorphous and the B block is crystalline and comprises a side chain comprising crystallizable moieties which render the block crystalline.
 13. A PSA composite according to claim 1 wherein each of the A blocks is crystalline and comprises a side chain comprising crystallizable moieties which render the block crystalline, and the B block is amorphous.
 14. A PSA composite according to claim 13 wherein the B block is a polyether polyacrylate, polyester, polyamide, polyurethane or polysiloxane block.
 15. An assembly which comprises(1) a first film which comprises a thermoplastic elastomer (TPE) comprising polymeric molecules which comprise(i) polymeric A blocks which(a) are crystalline and have a melting point T_(q), and (b) comprise side chain crystallizable moieties which render the block crystalline; and (ii) at least one polymeric B block which(a) is linked to at least two A blocks, (b) is amorphous at temperatures at which the TPE exhibits elastomeric behavior, (c) has a glass transition point T_(gs) which is less than (T_(q) -10)°C., and (d) is selected from the group consisting of polyethers, polyamides, polyurethanes and polysiloxanes; and (2) a second film which is heat-sealed to the first film and which is composed of a polymeric composition which is compatible with the A block or the B block or both.
 16. An assembly which comprises(A) a container comprising(1) a first film which comprises a thermoplastic elastomer (TPE) comprising polymeric molecules which comprise(i) polymeric A blocks which(a) are crystalline and have a melting point T_(q), or (b) are amorphous and have a glass transition point T_(gh) ; and (ii) at least one polymeric B block which is linked to at least two A blocks and which(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C., or (b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C.;wherein at least one block selected from the A and B blocks comprises a side chain comprising crystallizable moieties which render the block crystalline, and (2) a second film which is heat-sealed to the first film and which is composed of a polymeric composition which is compatible with the A block or the B block or both; and (B) a foodstuff which is hermetically sealed within the container.
 17. An assembly comprising(1) a first film which comprises a thermoplastic elastomer (TPE) comprisingpolymeric molecules which comprise (i) polymeric A blocks which(a) are crystalline and have a melting point T_(q), or (b) are amorphous and have a glass transition point T_(gh) ; and (ii) at least one polymeric B block which is linked to at least two A blocks and which(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C. or (b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C.wherein at least one block selected from the A and B blocks comprises a side chain comprising crystallizable moieties which render the block crystalline, the A blocks or the B blocks comprising 80-100% by weight of units derived from an n-alkyl acrylate, n-alkyl methacrylate, or n-alkyl methacrylamide, in which the alkyl group contains 18 to 30 carbon atoms, and (2) a second film which is heat-sealed to the first film and which is composed of a polymer or polymer blend which (i) contains at least 50% by weight of units derived from ethylene and (ii) is compatible with the A block or the B block or both.
 18. A process for joining two articles together which comprises forming a layer of a molten polymeric composition between the articles and pushing the articles together, and allowing the composition to cool, wherein the composition comprises a thermoplastic elastomer (TPE) comprising polymeric molecules which comprise(i) polymeric A blocks which(a) are crystalline and have a melting point T_(q), or (b) are amorphous and have a glass transition point T_(gh) ; (ii) at least one polymeric B block which is linked to at least two A blocks and which(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C. or (b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. or less than (T_(gh) -10)°C.wherein at least one block selected from the A and B blocks comprises a side chain comprising crystallizable moieties which render the block crystalline; and at least one of said articles is composed of a polymeric material which is compatible with the A block or the B block or both.
 19. A process according to claim 18 wherein each of the A blocks is amorphous, and the B block is crystalline and comprises a side chain comprising crystallizable moieties which render the block crystalline.
 20. A process according to claim 18 wherein each of the A blocks is crystalline and comprises a side chain comprising crystallizable moieties which render the block crystalline, and the B block is amorphous.
 21. A process for releasing a second component from a composition, shaped article or assembly which comprises(1) A thermoplastic elastomer (TPE) comprising polymeric molecules which comprise(i) at least two polymeric A blocks,(a) each of the A blocks being crystalline and having a melting point T_(q), and (b) at least one of the A blocks comprising a side chain comprising crystallizable moieties which render the block crystalline: and (ii) at least one polymeric B block which is linked to at least two A blocks and which(a) is crystalline and has a melting point T_(ms) which is less than (T_(q) -10)°C., or (b) is amorphous and has a glass transition point T_(gs) which is less than (T_(q) -10)°C. and (2) a second component which is mixed with the TPE or which is surrounded by the TPE or which provides a substrate for the TPE;which process comprises heating the composition, article or assembly to a temperature at least equal to T_(q) by means of heat which is (i) generated artificially or (ii) generated by a mammalian body and/or (iii) is conveyed artificially to the composition, article or assembly.
 22. A process according to claim 21 wherein each of the A blocks is amorphous, and the B block is crystalline and comprises a side chain comprising crystallizable moieties which render the block crystalline.
 23. A process according to claim 21 wherein each of the A blocks is crystalline and comprises a side chain comprising crystallizable moieties which render the block crystalline, and the B block is amorphous.
 24. A process according to claim 23 wherein the B block is a polyether, polyacrylate, polyester, polyamide, polyurethane or polysiloxane block.
 25. A package which comprises a foodstuff or biological material which is actively respiring and a container therefor, at least a part of said container being composed of a block copolymer of a side-chain crystallizable polymer and a second polymer which exhibits a glass transition or melting point higher than the side-chain crystallizable polymer. 